Surfactants free synthesis of superparamagnetic magnetite (Fe3O4) nanoparticles : Spectroscopic, magnetic and AFM studies

被引：0

作者：

Gautam, Ravindra Kumar ^{[1
]}

Banerjee, Sushmita ^{[1
]}

Gautam, Pavan Kumar ^{[1
]}

Jaiswal, Amita ^{[1
]}

Mani, Raj ^{[1
]}

Singh, Dharmveer ^{[1
]}

Pandey, J. D. ^{[1
]}

Chattopadhyaya, Mahesh Chandra ^{[1
]}

机构：

[1] Univ Allahabad, Dept Chem, Environm Chem Res Lab, Allahabad 211002, Uttar Pradesh, India

来源：

JOURNAL OF THE INDIAN CHEMICAL SOCIETY | 2016年 / 93卷 / 06期

关键词：

Magnetite nanoparticles; colloidal method; superparamagnetic; TEM; AFM; SQUID;

D O I：

暂无

中图分类号：

O6 [化学];

学科分类号：

0703 ;

摘要：

Superparamagnetic Fe3O4 nanoparticles with diameter of similar to 7 nm were prepared by a colloidal method, without employing surfactants and using precursors like FeCl3 center dot 6H(2)O, FeSO4 center dot 7H(2)O, deionized water and using NH4OH solution (29% vol.) as precipitating agent. The synthesized product was characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), scanning electron microscopy attached with energy dispersive X-ray (SEM-EDS), Fourier transform infrared spectroscopy (FT-IR), Brunauer-Emmett-Teller (BET) surface area, thermogravimetric analysis (TGA-DTG), and atomic force microscopy (AFM). The hysteresis loops of the magnetite nanoparticles were measured using a superconducting quantum interference device (SQUID) and the results showed a superparamagnetic behavior at room temperature.

引用

页码：649 / 654

页数：6

共 23 条

[11] In situ hybridization to chitosan/magnetite nanocomposite induced by the magnetic field [J].

Li, Baoqiang ;

Jia, Dechang ;

Zhou, Yu ;

Hu, Qiaoling ;

Cai, Wei .

JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2006, 306 (02) :223-227

[12] Preparation and characterization of magnetite nanoparticles coated by amino silane [J].

Ma, M ;

Zhang, Y ;

Yu, W ;

Shen, HY ;

Zhang, HQ ;

Gu, N .

COLLOIDS AND SURFACES A-PHYSICOCHEMICAL AND ENGINEERING ASPECTS, 2003, 212 (2-3) :219-226

[13] Synthesis of magnetite nanoparticles via a solvent-free thermal decomposition route [J].

Maity, Dipak ;

Choo, Shi-Guang ;

Yi, Jiabao ;

Ding, Jun ;

Xue, Jun Min .

JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2009, 321 (09) :1256-1259

[14] Modifying Fe3O4 nanoparticles with humic acid for removal of Rhodamine B in water [J].

Peng, Liang ;

Qin, Pufeng ;

Lei, Ming ;

Zeng, Qingru ;

Song, Huijuan ;

Yang, Jiao ;

Shao, Jihai ;

Liao, Bohan ;

Gu, Jidong .

JOURNAL OF HAZARDOUS MATERIALS, 2012, 209 :193-198

[15] A Fourier transform infrared (FTIR) and thermogravimetric analysis (TGA) study of oleate adsorbed on magnetite nano-particle surface [J].

Roonasi, Payman ;

Holmgren, Allan .

APPLIED SURFACE SCIENCE, 2009, 255 (11) :5891-5895

[16] A TGA-FTIR perspective of fatty acid adsorbed on magnetite nanoparticles-Decomposition steps and magnetite reduction [J].

Rudolph, Martin ;

Erler, Jacqueline ;

Peuker, Urs A. .

COLLOIDS AND SURFACES A-PHYSICOCHEMICAL AND ENGINEERING ASPECTS, 2012, 397 :16-23

[17] Monodisperse FePt nanoparticles and ferromagnetic FePt nanocrystal superlattices [J].

Sun, SH ;

Murray, CB ;

Weller, D ;

Folks, L ;

Moser, A .

SCIENCE, 2000, 287 (5460) :1989-1992

[18] Magnetic properties of nanocrystalline Fe3O4 films [J].

Tang, JK ;

Wang, KY ;

Zhou, WL .

JOURNAL OF APPLIED PHYSICS, 2001, 89 (11) :7690-7692

[19] Controlled-synthesis, characterization, and magnetic properties of Fe3O4 nanostructures [J].

Wan, J. ;

Yao, Y. ;

Tang, G. .

APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING, 2007, 89 (02) :529-532

[20] Preparation and magnetic properties of magnetite nanoparticles by sol-gel method [J].

Xu, Jing ;

Yang, Haibin ;

Fu, Wuyou ;

Du, Kai ;

Sui, Yongming ;

Chen, Jiuju ;

Zeng, Yi ;

Li, Minghui ;

Zou, Guangtian .

JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2007, 309 (02) :307-311

← 1 2 3 →