Effect of polymorphism of Al2O3 on the synthesis of magnesium aluminate spinel

被引：46

作者：

Zhang, ZH ^{[1
]}

Li, N ^{[1
]}

机构：

[1] Wuhan Univ Sci & Technol, Hubei Prov Key Lab Refractories & Ceram, Wuhan 430081, Hubei, Peoples R China

来源：

CERAMICS INTERNATIONAL | 2005年 / 31卷 / 04期

关键词：

sintering; alumina; magnesium aluminate spinel; densification;

D O I：

10.1016/j.ceramint.2004.06.025

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

MgAl2O4 spinet was prepared by reaction sintering and the effect of polymorphism of Al2O3 on the synthesis and densification of the spinet studied. gamma-Al2O3, rho-Al2O3 and alpha-Al2O3 were mixed with analytical reagent of MgO according to the stoichiometric spinet ratio, respectively, and pressed into billets with diameter of 20 mm and height of 15 mm. The green-body billets then were sintered at temperature from 800 degrees C to 1600 degrees C in an air atmosphere. Bulk density, porosity, linear expansion changes, phase composition, microstructure and grain size of final sintered products were analyzed. The results indicated that gamma-Al2O3 is beneficial for synthesize of spinet because it has a crystal structure similar to that of spine]. Among materials sintered at 1600 degrees C for 3 h, samples using gamma-Al2O3 as raw material had the highest density, up to 91% of the theoretical density of MgAl2O4, and had the largest grain size of spinel. (c) 2004 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

引用

页码：583 / 589

页数：7

共 50 条

[41] EFFECT OF SULFIDING TEMPERATURES ON THE FORMATION OF SULFIDES OF MO/AL2O3 AND COMO/AL2O3 [J].

SEO, IK ;

SEONG, IW .

APPLIED CATALYSIS, 1991, 74 (01) :109-123

[42] Effect of raw materials on formation and densification of magnesium aluminate spinel [J].

Sarkar, Ritwik ;

Sahoo, Sachin .

CERAMICS INTERNATIONAL, 2014, 40 (10) :16719-16725

[43] SYNTHESIS OF MAGNESIUM ALUMINATE SPINEL DOPED TiO2 FROM MAGNESITE WASTE [J].

Canikoglu, N. .

ARCHIVES OF METALLURGY AND MATERIALS, 2022, 67 (01) :311-316

[44] EFFECT OF CHLORIDE ON SINTERING OF PT/AL2O3 CATALYSTS [J].

BARBIER, J ;

BAHLOUL, D ;

MARECOT, P .

CATALYSIS LETTERS, 1991, 8 (5-6) :327-334

[45] Effect of Al2O3 on the sinterability of fine zirconia powder [J].

Matsui, K ;

Etoh, N ;

Ohgai, M ;

Uehara, M ;

Enomoto, N ;

Hojo, J .

EURO CERAMICS VII, PT 1-3, 2002, 206-2 :345-348

[46] Effect of YSZ with different Y2O3 contents on toughening behavior of Al2O3/Ba-β-Al2O3/ZrO2 composites [J].

Liu, Lei ;

Maeda, Kensaku ;

Onda, Tetsuhiko ;

Chen, Zhong-Chun .

CERAMICS INTERNATIONAL, 2019, 45 (14) :18037-18043

[47] Sintering behaviour and microstructures of Ti(Al,O)/Al2O3, Ti3Al(O)/Al2O3 and TiAl(O)/Al2O3 in situ composites [J].

Cai, ZH ;

Zhang, DL .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 419 (1-2) :310-317

[48] Effect of grain size on the static and dynamic mechanical properties of magnesium aluminate spinel (MgAl2O4) [J].

Sokol, M. ;

Kalabukhov, S. ;

Shneck, R. ;

Zaretsky, E. ;

Frage, N. .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2017, 37 (10) :3417-3424

[49] Effect of TiO2 on Mechanical Properties and Microstructure of Magnesium Aluminate Spinel Refractories [J].

Wei, Juncong ;

Han, Xiaocui ;

Gao, Chunhui ;

Huang, Jiankun ;

Tu, Junbo .

MATERIALS AND DESIGN, PTS 1-3, 2011, 284-286 :638-641

[50] Effect of Y2O3 doping on the high-temperature properties of magnesia aluminate spinel refractories [J].

Liu, Jiangbo ;

Wang, Zhoufu ;

Liu, Hao ;

Wang, Xitang ;

Ma, Yan .

JOURNAL OF THE AUSTRALIAN CERAMIC SOCIETY, 2020, 56 (02) :389-394

← 1 2 3 4 5 →