Effect of polymorphism of Al2O3 on the synthesis of magnesium aluminate spinel

被引：46
作者：
Zhang, ZH [1 ]
Li, N [1 ]
机构：
[1] Wuhan Univ Sci & Technol, Hubei Prov Key Lab Refractories & Ceram, Wuhan 430081, Hubei, Peoples R China
来源：
CERAMICS INTERNATIONAL | 2005年 / 31卷 / 04期
关键词：
sintering; alumina; magnesium aluminate spinel; densification;
D O I：
10.1016/j.ceramint.2004.06.025
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
MgAl2O4 spinet was prepared by reaction sintering and the effect of polymorphism of Al2O3 on the synthesis and densification of the spinet studied. gamma-Al2O3, rho-Al2O3 and alpha-Al2O3 were mixed with analytical reagent of MgO according to the stoichiometric spinet ratio, respectively, and pressed into billets with diameter of 20 mm and height of 15 mm. The green-body billets then were sintered at temperature from 800 degrees C to 1600 degrees C in an air atmosphere. Bulk density, porosity, linear expansion changes, phase composition, microstructure and grain size of final sintered products were analyzed. The results indicated that gamma-Al2O3 is beneficial for synthesize of spinet because it has a crystal structure similar to that of spine]. Among materials sintered at 1600 degrees C for 3 h, samples using gamma-Al2O3 as raw material had the highest density, up to 91% of the theoretical density of MgAl2O4, and had the largest grain size of spinel. (c) 2004 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
引用
收藏
页码：583 / 589
页数：7
相关论文
共 50 条
[31]   Synthesis and Photoluminescence of γ-Al2O3 and C-doped γ-Al2O3 Powders [J].
Wang, S. F. ;
Zhuang, C. F. ;
Yuan, Y. G. ;
Xiang, X. ;
Sun, G. Z. ;
Ding, Q. P. ;
Li, Z. J. ;
Zu, X. T. .
TRANSACTIONS OF THE INDIAN CERAMIC SOCIETY, 2014, 73 (01) :37-42
[32]   Function of magnesium aluminate hydrate and magnesium nitrate as MgO addition in crystal structure and grain size control of α-Al2O3 during sintering [J].
Soumen Pal ;
A. K. Bandyopadhyay ;
S. Mukherjee ;
B. N. Samaddar ;
P. G. Pal .
Bulletin of Materials Science, 2010, 33 :55-63
[33]   Function of magnesium aluminate hydrate and magnesium nitrate as MgO addition in crystal structure and grain size control of α-Al2O3 during sintering [J].
Pal, Soumen ;
Bandyopadhyay, A. K. ;
Mukherjee, S. ;
Samaddar, B. N. ;
Pal, P. G. .
BULLETIN OF MATERIALS SCIENCE, 2010, 33 (01) :55-63
[34]   Effect of spinning solution parameters on synthesis of magnesium aluminate spinel fibers via electrospinning [J].
Cui Y. ;
Wei H. ;
Wang H. ;
Wei Y. ;
Lin J. ;
Bu J. ;
Wang P. .
Cailiao Yanjiu Xuebao/Chinese Journal of Materials Research, 2016, 30 (02) :115-122
[35]   Hydrothermal synthesis and intrinsic luminescent properties of magnesium aluminate spinel [J].
Lu, Yang ;
Wang, Jing ;
He, Lijie ;
Shi, Zhongxiang ;
Wang, Xin ;
Zhao, Keting .
JOURNAL OF ALLOYS AND COMPOUNDS, 2025, 1010
[36]   Optically stimulated luminescence of magnesium aluminate (MgAl2O4) spinel [J].
Yoshimura, EM ;
Yukihara, EG .
RADIATION MEASUREMENTS, 2006, 41 (02) :163-169
[37]   Effect of polymorphism of Al2O3 on the sintering and microstructure of transparent MgAl2O4 ceramics [J].
Han, Dan ;
Zhang, Jian ;
Liu, Peng ;
Wang, Shiwei .
OPTICAL MATERIALS, 2017, 71 :62-65
[38]   Two-step sintering of magnesium aluminate spinels and their corrosion in Na3AlF6-AlF3-CaF2-Al2O3 bath [J].
Liu, Jian-hua ;
Lu, Xiao-jun ;
Li, Jie ;
Hu, Ling-yun ;
Jiang, Liang-xing .
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2016, 26 (10) :2754-2761
[39]   The effect of ZnO addition on the densification and properties of magnesium aluminate spinel [J].
Ghosh, A ;
Das, SK ;
Biswas, JR ;
Tripathi, HS ;
Banerjee, G .
CERAMICS INTERNATIONAL, 2000, 26 (06) :605-608
[40]   Mechanochemical synthesis of α-Al2O3-Cr3+ (Ruby) and χ-Al2O3 [J].
Cortes-Vega, Fernando D. ;
Yang, Wenli ;
Zarate-Medina, Juan ;
Brankovic, Stanko R. ;
Calderon, Hector A. ;
Hernandez, Francisco C. Robles .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2019, 102 (03) :976-980
12345