Comparison of corrosion behaviour of zinc in NaCl and in NaOH solutions. Part I: Corrosion layer characterization

被引：161
作者：
Mouanga, M. [1 ]
Bercot, P. [1 ]
Rauch, J. Y. [2 ]
机构：
[1] Univ Franche Comte, Equipe Sonochim & React Surfaces, CNRS, Inst UTINAM,UMR 6213, F-25030 Besancon, France
[2] Univ Franche Comte, FEMTO ST, F-25030 Besancon, France
来源：
CORROSION SCIENCE | 2010年 / 52卷 / 12期
关键词：
Zinc; Corrosion products; XRD; XPS; PULSE-CURRENT ELECTRODEPOSITION; ATMOSPHERIC CORROSION; PROTECTIVE ABILITY; ZN; DEPOSITION; COATINGS; COUMARIN; ALLOYS; STEEL;
D O I：
10.1016/j.corsci.2010.08.003
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The corrosion layer formed on zinc sample in 0.6 M NaCl and 0.5 M NaOH solution under ambient conditions has been investigated. The corrosion layer morphology was analyzed using scanning electron microscopy (SEM). X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) were used to characterize the corrosion products of zinc. The thickness evolution of the corrosion layer was investigated by glow discharge optical emission spectroscopy (GDEOS). The corrosion layer formed in 0.5 M NaOH solution appeared more compact than that formed in 0.6 M NaCl solution. Zinc hydroxide chloride (Zn(5)(OH)(8)Cl(2)center dot 2H(2)O) and zinc hydroxide carbonate (Zn(5)(CO(3))(2)(OH)(6)) were formed on zinc surface in 0.6 M NaCl solution while in 0.5 M NaOH solution, zinc oxide (ZnO), zinc hydroxide (Zn(OH)(2)) and zinc hydroxide carbonate (Zn(5)(OH)(6)(CO(3))(2)center dot H(2)O) were detected. Probable mechanisms of zinc corrosion products formation are presented. (C) 2010 Elsevier Ltd. All rights reserved.
引用
收藏
页码：3984 / 3992
页数：9
相关论文
共 18 条
[1]  
[Anonymous], DATABASE SURFACE SPE
[2]   Effects of organic inhibitors on corrosion of zinc in an aerated 0.5 M NaCl solution [J].
Aramaki, K .
CORROSION SCIENCE, 2001, 43 (10) :1985-2000
[3]   Galvanic Zn-Mn alloys - electrodeposition, phase composition, corrosion behaviour and protective ability [J].
Boshkov, N .
SURFACE & COATINGS TECHNOLOGY, 2003, 172 (2-3) :217-226
[4]   Composition of the corrosion products of galvanic alloys Zn-Co and their influence on the protective ability [J].
Boshkov, N ;
Petrov, K ;
Vitkova, S ;
Nemska, S ;
Raichevsky, G .
SURFACE & COATINGS TECHNOLOGY, 2002, 157 (2-3) :171-178
[5]   Initial NaCl-particle induced atmospheric corrosion of zinc-effect of CO2 and SO2 [J].
Chen, Z. Y. ;
Persson, D. ;
Leygraf, C. .
CORROSION SCIENCE, 2008, 50 (01) :111-123
[6]   XPS study of the surface chemistry of conventional hot-dip galvanised pure Zn, galvanneal and Zn-Al alloy coatings on steel [J].
Feliu, S ;
Barranco, V .
ACTA MATERIALIA, 2003, 51 (18) :5413-5424
[7]   Corrosion resistance of zinc-magnesium coated steel [J].
Hosking, N. C. ;
Strom, M. A. ;
Shipway, P. H. ;
Rudd, C. D. .
CORROSION SCIENCE, 2007, 49 (09) :3669-3695
[8]  
*INT CTR DIFFR DAT, JCPDS ICDD MIN POWD
[9]   Zinc photo-corrosion in neutral solutions [J].
Kalinauskas, P ;
Valsiunas, I ;
Samuleviciene, M ;
Juzeliunas, E .
CORROSION SCIENCE, 2001, 43 (11) :2083-2092
[10]   Influence of coumarin on zinc electrodeposition [J].
Mouanga, M. ;
Ricq, L. ;
Douglade, G. ;
Douglade, J. ;
Bercot, P. .
SURFACE & COATINGS TECHNOLOGY, 2006, 201 (3-4) :762-767
12