Stress Oriented Hydrogen Induced Cracking of Linepipe Steel

被引：0

作者：

Kim, Wan Keun ^{[1
]}

Park, Gyu Tae ^{[1
]}

Kim, Kyoo Young ^{[1
]}

机构：

[1] Pohang Univ Sci & Technol, Grad Inst Ferrous Technol, Pohang 790784, South Korea

来源：

JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL | 2011年 / 18卷

关键词：

linepipe steel; stress oriented hydrogen induced cracking; hydrogen induced cracking; metallurgical factor; diffusible hydrogen; LOW-ALLOY STEELS; SOUR ENVIRONMENTS; PIPELINE STEELS; HIGH-STRENGTH; SUSCEPTIBILITY; EMBRITTLEMENT; PERMEATION; MOLYBDENUM; RESISTANCE; IRON;

D O I：

暂无

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

The stress oriented hydrogen induced cracking (SOHIC) is a typical hydrogen embrittlement phenomenon occurring in the linepipe steels exposed to sour environment containing H(2)S gas. However, even recently, the cracking mechanism of SONIC has not been clarified because of lacking in the empirical data on the actual failure mode of SOH IC cracking. The factors affecting SOH IC are discussed in terms of metallurgy of high strength linepipe steel and hydrogen electrochemistry. The cracking mechanisms of SOHIC are examined by comparing them with the empirical failure mode of SOHIC which is developed by observation of the actual fracture sites of the hydrogen induced blister cracking (HIBC) and secondary cracks. Finally, the correlation between SOHIC and HIC is discussed.

引用

页码：121 / 128

页数：8

共 50 条

[31] Investigation of the effect of electrolytic hydrogen charging of X70 steel: I. The effect of microstructure on hydrogen-induced cold cracking and blistering
Dunne, Druce P.
Hejazi, Daniel
Saleh, Ahmed A.
Haq, Ayesha J.
Calka, Andrzej
Pereloma, Elena V.
INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2016, 41 (28) : 12411 - 12423
[32] Hydrogen blistering and cracking of high-strength pipeline steel welds produced by electrochemical hydrogen charging
Lan, Liangyun
Zhang, Yiting
Chang, Zhiyuan
Li, Huixing
Yin, Jiyao
Atrens, Andrej
MATERIALIA, 2024, 34
[33] Hydrogen Stress Cracking Behaviour in Dissimilar Welded Joints of Duplex Stainless Steel and Carbon Steel
Park, Hanji
Moon, Byungrok
Moon, Younghoon
Kang, Namhyun
METALS, 2021, 11 (07)
[34] Role of cold rolled followed by annealing on improvement of hydrogen induced cracking resistance in pipeline steel
Mohtadi-Bonab, M. A.
Eskandari, M.
Szpunar, J. A.
ENGINEERING FAILURE ANALYSIS, 2018, 91 : 172 - 181
[35] Evaluation of Hydrogen-induced Cracking Behavior in Duplex Stainless Steel by Numerical Simulation of Stress and Diffusible Hydrogen Distribution at the Microstructural Scale
Ogita, Gen
Matsumoto, Koki
Mochizuki, Masahito
Mikami, Yoshiki
Ito, Kazuhiro
TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 2020, 106 (04): : 214 - 223
[36] THE EFFECT OF HYDROGEN-INDUCED CRACKING ON THE INTEGRITY OF STEEL-COMPONENTS
CHATTORAJ, I
SADHANA-ACADEMY PROCEEDINGS IN ENGINEERING SCIENCES, 1995, 20 : 199 - 211
[37] Effects of vanadium precipitates on hydrogen trapping efficiency and hydrogen induced cracking resistance in X80 pipeline steel
Li, Longfei
Song, Bo
Cheng, Jin
Yang, Zhanbing
Cai, Zeyun
INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2018, 43 (36) : 17353 - 17363
[38] INFLUENCE OF SOFTENED HEAT-AFFECTED ZONE ON STRESS ORIENTED HYDROGEN-INDUCED CRACKING OF A HIGH-STRENGTH LINE PIPE STEEL
TAKAHASHI, A
OGAWA, H
ISIJ INTERNATIONAL, 1995, 35 (10) : 1190 - 1195
[39] Effects of alloying elements and microstructure on the susceptibility of the welded HSLA steel to hydrogen-induced cracking and sulfide stress cracking
Beidokhti, B.
Dolati, A.
Koukabi, A. H.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2009, 507 (1-2): : 167 - 173
[40] Combined impact of elastic stress, prestrain and electrochemical charging on the hydrogen-induced cracking of high-strength steel
Hu, Songyan
Tian, Zhiqiang
Wang, Yafei
Hu, Haijun
Li, Xiufeng
Liu, Qian
Liu, Dongpeng
Li, Yun
Cheng, Guangxu
INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2023, 48 (39) : 14923 - 14929

← 1 2 3 4 5 →