Elevated temperature compressive behavior of in-situ multiphase composites NiAl/Cr(Mo)-TiC

被引:20
作者
Jiang, DT [1 ]
Guo, JT [1 ]
机构
[1] Chinese Acad Sci, Inst Met Res, Shenyang 110015, Peoples R China
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 1998年 / 255卷 / 1-2期
关键词
deformation; NiAl; particulate composite; reaction synthesis;
D O I
10.1016/S0921-5093(98)00671-6
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
A new multiphase composite based on intermetallic NiAl was fabricated using reaction synthesis method. The TiC particles were formed in-situ in the matrix and most of them accumulated at phase or grain boundaries. Its elevated temperature compressive behavior was investigated. The flow stresses of the composites generally decreased with increasing temperature and/or decreasing initial strain rate. It was found that the deformation feature of the composites could be adequately described by standard power law which is usually used to characterize creep behavior for various metallic materials. Thus the stress exponent n as well as activation energy Q were calculated by fitting the experimental data to the power-law and temperature-compensated power-law equations. The deformation behavior was discussed in comparison with other NiAl matrix composites. The high temperature strengths of the composites, especially the 16wt.%TiC particulate reinforced one, are superior to monolithic NiAl and a composite NiAl-20vol.%TiB2 at slower strain rate. The strengthening mechanisms were discussed preliminarily. However, when compared with directionally solidified NiAl/Cr(Mo), the present composites are relatively weak. An explanation for the weakness is given in the paper. (C) 1998 Elsevier Science S.A. All rights reserved.
引用
收藏
页码:154 / 161
页数:8
相关论文
共 34 条
[21]  
NOEBE RD, 1991, INTERMETALLIC MATRIX, V194, P323
[22]   SELF-PROPAGATING HIGH-TEMPERATURE SYNTHESIS [J].
SUBRAHMANYAM, J ;
VIJAYAKUMAR, M .
JOURNAL OF MATERIALS SCIENCE, 1992, 27 (23) :6249-6273
[23]   EFFECT OF SOLIDIFICATION RATE ON STRUCTURE AND HIGH-TEMPERATURE STRENGTH OF EUTECTIC NIAL-CR [J].
WALTER, JL ;
CLINE, HE .
METALLURGICAL TRANSACTIONS, 1970, 1 (05) :1221-&
[24]   MICROSTRUCTURE OF TIB2-NIAL [J].
WANG, L ;
ARSENAULT, RJ .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1990, 127 (01) :91-98
[25]   ELEVATED-TEMPERATURE CREEP-PROPERTIES OF NIAL CRYOMILLED WITH AND WITHOUT Y2O3 [J].
WHITTENBERGER, JD ;
LUTON, MJ .
JOURNAL OF MATERIALS RESEARCH, 1995, 10 (05) :1171-1186
[26]   ELEVATED-TEMPERATURE SLOW PLASTIC-DEFORMATION OF NIAL-TIB2 PARTICULATE COMPOSITES AT 1200-K AND 1300-K [J].
WHITTENBERGER, JD ;
VISWANADHAM, RK ;
MANNAN, SK ;
SPRISSLER, B .
JOURNAL OF MATERIALS SCIENCE, 1990, 25 (1A) :35-44
[27]   PRELIMINARY INVESTIGATION OF A NIAL COMPOSITE PREPARED BY CRYOMILLING [J].
WHITTENBERGER, JD ;
ARZT, E ;
LUTON, MJ .
JOURNAL OF MATERIALS RESEARCH, 1990, 5 (02) :271-277
[28]   SLOW PLASTIC-DEFORMATION OF EXTRUDED NIAI-10TIB2 PARTICULATE COMPOSITES AT 1200-K AND 1300-K [J].
WHITTENBERGER, JD ;
KUMAR, S ;
MANNAN, SK ;
VISWANADHAM, RK .
JOURNAL OF MATERIALS SCIENCE LETTERS, 1990, 9 (03) :326-328
[29]   COMPRESSIVE STRENGTH OF A B2 MATRIX NIAL-NB INTERMETALLIC AT 1200-K AND 1300-K [J].
WHITTENBERGER, JD ;
WESTFALL, LJ ;
NATHAL, MV .
SCRIPTA METALLURGICA, 1989, 23 (12) :2127-2130
[30]   COMPRESSIVE STRENGTH OF DIRECTIONALLY SOLIDIFIED NIAL-NIALNB INTERMETALLICS AT 1200-K AND 1300-K [J].
WHITTENBERGER, JD ;
REVIERE, R ;
NOEBE, RD ;
OLIVER, BF .
SCRIPTA METALLURGICA ET MATERIALIA, 1992, 26 (06) :987-992