Electrophoretic deposition of CoFe2O4 films from aqueous suspensions

被引：6
作者：
Jian, Gang [1 ]
Zhao, Jun [1 ]
Zhou, Dongxiang [1 ]
Fu, Qiuyun [1 ]
机构：
[1] Huazhong Univ Sci & Technol, Dept Elect Sci & Technol, Wuhan 430074, Hubei, Peoples R China
来源：
CERAMICS INTERNATIONAL | 2012年 / 38卷 / 05期
基金：
中国国家自然科学基金;
关键词：
Suspensions; Electrophoretic deposition; CoFe2O4; Preferential orientations; THIN-FILMS; MAGNETIC-PROPERTIES; FOILS;
D O I：
10.1016/j.ceramint.2012.01.014
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
CoFe2O4 nano-particles with average size of similar to 40 nm were synthesized via the chemical coprecipitation method. PAMA-NH4 was used as dispersant to improve the stability of aqueous suspensions. Zeta potential and sediment volumes were tested to study the effects of pH and dispersant amounts on the stability of suspensions. The most stable suspension was obtained when using 0.6 wt.% PAMA-NH4 as dispersant at pH = 10. Conductivity results showed that thoroughly dispersed suspensions were formed after being ultrasonic agitated for 30 min. CoFe2O4 films on Al2O3/Pt substrates fabricated via EPD sintered at 1250 degrees C exhibited preferentially oriented structure. The XRD analyses showed (2 2 0) and (5 1 1) were the preferential orientations. Anisotropy was also observed in magnetic hysteresis loops. Stronger ferromagnetic effect was observed in the in-plane orientation, with saturation magnetization of similar to 290 emu/cm(3). (C) 2012 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
引用
收藏
页码：3707 / 3711
页数：5
相关论文
共 14 条
  • [1] ZETA-POTENTIAL AND SEDIMENTATION BEHAVIOUR IN FLOCCULATED CANE SUGAR JUICE
    BENNETT, MC
    [J]. NATURE, 1958, 182 (4647) : 1439 - 1440
  • [2] Determination and control of metallic impurities in alumina deposits obtained by aqueous electrophoretic deposition
    Ferrari, B
    Fariñas, JC
    Moreno, R
    [J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2001, 84 (04) : 733 - 739
  • [3] Microstructure and Properties of Well-Ordered Multiferroic Pb(Zr,Ti)O3/CoFe2O4 Nanocomposites
    Gao, Xingsen
    Rodriguez, Brian J.
    Liu, Lifeng
    Birajdar, Balaji
    Pantel, Daniel
    Ziese, Michael
    Alexe, Marin
    Hesse, Dietrich
    [J]. ACS NANO, 2010, 4 (02) : 1099 - 1107
  • [4] Surface morphology and magnetic properties of CoFe2O4 thin films grown by a RF magnetron sputtering method
    Lee, JG
    Chae, KP
    Sur, JC
    [J]. JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2003, 267 (02) : 161 - 167
  • [5] Magnetic anisotropy and domain structure in epitaxial CoFe2O4 thin films
    Lisfi, A
    Williams, CM
    [J]. JOURNAL OF APPLIED PHYSICS, 2003, 93 (10) : 8143 - 8145
  • [6] Electric and Magnetic Properties of CoFe2O4-PbZr0.5Ti0.5O3 Composite Thin Films
    Mo, Weifeng
    Zhai, Jiwei
    Zhang, Ling
    Yao, Xi
    [J]. FERROELECTRICS, 2010, 407 : 54 - 60
  • [7] Structure and magnetic characterizations of cobalt ferrite films prepared by spray pyrolysis
    Phua, L. X.
    Xu, F.
    Ma, Y. G.
    Ong, C. K.
    [J]. THIN SOLID FILMS, 2009, 517 (20) : 5858 - 5861
  • [8] Electrophoretic deposition of aqueous nano-sized zinc oxide suspensions on a zinc electrode
    Tang, FQ
    Sakka, Y
    Uchikoshi, T
    [J]. MATERIALS RESEARCH BULLETIN, 2003, 38 (02) : 207 - 212
  • [9] High-coercivity Co-ferrite thin films on (100)-SiO2 substrate
    Wang, YC
    Ding, J
    Yi, JB
    Liu, BH
    Yu, T
    Shen, ZX
    [J]. APPLIED PHYSICS LETTERS, 2004, 84 (14) : 2596 - 2598
  • [10] Microstructural studies of PZT thick films on Cu foils
    Wu, Aiying
    Vilarinho, P. M.
    Srinivasan, S.
    Kingon, A. I.
    Reaney, I. M.
    Woodward, D.
    Ramos, A. R.
    Alves, E.
    [J]. ACTA MATERIALIA, 2006, 54 (12) : 3211 - 3220
12