Microporosity and connections between pores in SBA-15 mesostructured silicas as a function of the temperature of synthesis

被引：489
作者：
Galarneau, A
Cambon, N
Di Renzo, F
Ryoo, R
Choi, M
Fajula, F
机构：
[1] Ecole Natl Super Chim Montpellier, Lab Mat Catalyt & Catalyse Chim Organ, CNRS, UMR 5618, F-34296 Montpellier 5, France
[2] Korea Adv Inst Sci & Technol, Dept Chem, Natl Creat Res Initiat Ctr Funct Mat, Sch Mol Sci BK21, Taejon 305701, South Korea
来源：
NEW JOURNAL OF CHEMISTRY | 2003年 / 27卷 / 01期
关键词：
D O I：
10.1039/b207378c
中图分类号：
O6 [化学];
学科分类号：
0703 ;
摘要：
Imaging of the platinum replica of the porous structure and low-pressure argon adsorption allowed us to elucidate the complicated porous structure of SBA-15. These techniques enabled us to draw a coherent picture of the evolution of the SBA-15 precursor mesophase as a function of the synthesis temperature. TEM of the platinum replicas has been unable to show bridges between the structural mesopores of SBA-15 synthesized at low temperature, whereas mesoporous bridges are clearly observed for samples formed at higher temperature. Argon adsorption has evidenced the ultramicroporosity of the materials formed at low temperature, as well as its evolution to secondary porosity with diameters greater than 1.5 nm under more severe hydrothermal treatment.
引用
收藏
页码：73 / 79
页数：7
相关论文
共 32 条
  • [1] Booth C, 2000, MACROMOL RAPID COMM, V21, P501, DOI 10.1002/1521-3927(20000601)21:9<501::AID-MARC501>3.0.CO
  • [2] 2-R
  • [3] IMPROVED STABILITY OF MCM-41 THROUGH TEXTURAL CONTROL
    COUSTEL, N
    DIRENZO, F
    FAJULA, F
    [J]. JOURNAL OF THE CHEMICAL SOCIETY-CHEMICAL COMMUNICATIONS, 1994, (08) : 967 - 968
  • [4] STUDIES ON PORE SYSTEMS IN CATALYSTS .6. UNIVERSAL T CURVE
    DEBOER, JH
    LINSEN, BG
    OSINGA, TJ
    [J]. JOURNAL OF CATALYSIS, 1965, 4 (06) : 643 - &
  • [5] DESPLANTIERGISC.D, 2000, STUD SURF SCI CATAL, V129, P665
  • [6] DESPLANTIERGISC.D, 2001, STUD SURF SCI CATAL, V135, P205
  • [7] Di Renzo F, 2002, STUD SURF SCI CATAL, V142, P1057
  • [8] Mesotunnels on the silica wall of ordered SBA-15 to generate three-dimensional large-pore mesoporous networks
    Fan, J
    Yu, CZ
    Wang, LM
    Tu, B
    Zhao, DY
    Sakamoto, Y
    Terasaki, O
    [J]. JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 2001, 123 (48) : 12113 - 12114
  • [9] Comparative textural study of highly ordered silicate and aluminosilicate mesoporous mesophase materials having different pore sizes
    Fenelonov, VB
    Derevyankin, AY
    Kirik, SD
    Solovyov, LA
    Shmakov, AN
    Bonardet, JL
    Gedeon, A
    Romannikov, VN
    [J]. MICROPOROUS AND MESOPOROUS MATERIALS, 2001, 44 : 33 - 40
  • [10] MODEL STRUCTURES FOR MCM-41 MATERIALS - A MOLECULAR-DYNAMICS SIMULATION
    FEUSTON, BP
    HIGGINS, JB
    [J]. JOURNAL OF PHYSICAL CHEMISTRY, 1994, 98 (16) : 4459 - 4462
1234