A two-step synthesis of well-ordered cubic mesoporous silica materials under mildly acidic conditions

被引:10
|
作者
Jin, Zhengwei [1 ]
Wang, Xiaodong [1 ]
Cui, Xiuguo [2 ]
机构
[1] Beijing Univ Chem Technol, Sch Mat Sci & Engn, Key Lab Beijing City Preparat & Proc Novel Polyme, Beijing 100029, Peoples R China
[2] Yanbian Univ, Dept Chem Engn & Polymer Sci, Yanji 133002, Jilin, Peoples R China
关键词
mesoporous silica materials; mildly acidic conditions; two-step synthesis; characterization;
D O I
10.1016/j.micromeso.2007.03.042
中图分类号
O69 [应用化学];
学科分类号
081704 ;
摘要
Well-ordered mesoporous silica materials were synthesized by using poly(ethylene oxide-b-propylene oxide-b-ethylene oxide) triblock copolymer as template through two-step pathway under mildly acidic conditions (pH 2.2-4.1). The highly ordered cage-like mesoporosity of the prepared materials having cubic Fm3m mesostructure was evidenced by the well-defined small angle X-ray diffraction patterns combined with transmission electron microscopy. Scanning electron microscopy observation exhibits a macron-sized spherical morphological structure for the prepared materials at pH 2.2, and a variation trend to small amount of spheres on the surface of randomly shaped agglomerations with increasing the pH value. The nitrogen adsorption-desorption analysis reveals that the prepared mesoporous silica materials have a uniform moderate-sized pore diameter (5.6-6.5 nm) and a very thick pore wall (4.96-6.10 nm). These features may lead to a much higher thermal, hydrothermal, and mechanical stability. The mesoporous silica materials synthesized in this study will favor the incorporation of catalytically active heteroatoms in silica frameworks, and the functionalization of organic groups for applications in catalysis, sensor and separation. The two-step synthetic method under mildly acidic conditions can also be extended to the production in the industrial scale as an environmentally friendly way. (c) 2007 Elsevier Inc. All rights reserved.
引用
收藏
页码:183 / 192
页数:10
相关论文
共 50 条
  • [31] Scattering effect of the well-ordered MgB4 impurity phase in two-step sintered polycrystalline MgB2 with glycine addition
    Cai, Qi
    Liu, Yongchang
    Guo, Qianying
    Ma, Zongqing
    APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING, 2017, 123 (04):
  • [32] A mild and convenient one-pot two-step synthesis of hydroxyiminodihydrobenzofurans mediated by silica gel under microwave activation conditions
    Barange, Deepak Kumar
    Raju, B. Rama
    Kavala, Veerababurao
    Kuo, Chun-Wei
    Tu, Yu-Chen
    Yao, Ching-Fa
    TETRAHEDRON, 2010, 66 (21) : 3754 - 3760
  • [33] From Anilines to Aziridines: A Two-Step Synthesis under Continuous-Flow Conditions
    Rossi, Sergio
    Puglisi, Alessandra
    Intrieri, Daniela
    Gallo, Emma
    JOURNAL OF FLOW CHEMISTRY, 2016, 6 (03) : 234 - 239
  • [34] From Anilines to Aziridines: A Two-Step Synthesis under Continuous-Flow Conditions
    Sergio Rossi
    Alessandra Puglisi
    Daniela Intrieri
    Emma Gallo
    Journal of Flow Chemistry, 2016, 6 : 234 - 239
  • [35] The search of promoters for silica condensation and rational synthesis of hydrothermally stable and well ordered mesoporous silica materials with high degree of silica condensation at conventional temperature
    Du, Yunchen
    Lan, Xijie
    Liu, Sen
    Ji, Yanyan
    Zhang, Yonglai
    Zhang, Weiping
    Xiao, Feng-Shou
    MICROPOROUS AND MESOPOROUS MATERIALS, 2008, 112 (1-3) : 225 - 234
  • [36] Synthesis of stable colloidal suspensions of ordered mesostructured silica from sodium metasilicate using pluronic P123 and mildly acidic conditions
    Berggren, Andreas
    Holmberg, Krister
    Palmqvist, Anders E. C.
    RECENT PROGRESS IN MESOSTRUCTURED MATERIALS, PROCEEDINGS OF THE 5TH INTERNATIONAL MESOSTRUCTURED MATERIALS SYMPOSIUM - IMMS2006, 2007, 165 : 53 - 56
  • [37] Direct hydrothermal synthesis of mesoporous Sn-SBA-15 materials under weak acidic conditions
    Shah, P.
    Ramaswamy, A. V.
    Lazar, K.
    Ramaswamy, Veda
    MICROPOROUS AND MESOPOROUS MATERIALS, 2007, 100 (1-3) : 210 - 226
  • [38] Zirconium-promoted hydrothermal synthesis of hierarchical porous carbons with ordered cubic mesostructures under acidic aqueous conditions
    Zhang, Anfeng
    Hou, Keke
    Duan, Haiyang
    Tan, Wei
    Song, Chunshan
    Guo, Xinwen
    RSC ADVANCES, 2016, 6 (06) : 4343 - 4353
  • [39] Application of an adsorption isotherm to explain incomplete drug release from ordered mesoporous silica materials under supersaturating conditions
    Dening, Tahnee J.
    Zemlyanov, Dmitry
    Taylor, Lynne S.
    JOURNAL OF CONTROLLED RELEASE, 2019, 307 : 186 - 199
  • [40] One-pot two-step synthesis of core-shell mesoporous silica-coated gold nanoparticles
    Song, Ji-Tao
    Zhang, Xiao-Shuai
    Qin, Meng-Yao
    Zhao, Yuan-Di
    DALTON TRANSACTIONS, 2015, 44 (17) : 7752 - 7756