Electroless deposition of thin-film cobalt-tungsten-phosphorus layers using tungsten phosphoric acid (H3[P(W3O10)4]) for ULSI and MEMS applications

被引:43
作者
Shacham-Diamand, Y [1 ]
Sverdlov, Y [1 ]
Petrov, N [1 ]
机构
[1] Tel Aviv Univ, Fac Engn, Dept Phys Elect, IL-69978 Tel Aviv, Israel
关键词
D O I
10.1149/1.1346605
中图分类号
O646 [电化学、电解、磁化学];
学科分类号
081704 ;
摘要
This paper describes an electroless deposition method for the formation of thin metallic films that contain mainly cobalt with significant amount of tungsten (up to similar to 11 atom % ) and phosphorus (in the range of 1-3 atom % ). The Ca(W, P) films can be applied for microelectronics multilevel metallization or for ultralage-scale integrated (ULSI) and microelectromechanical systems (MEMS) applications. The film was deposited from an aqueous electrolyte that contained tungsten phosphoric acid, H-3[P(W3O10)(4)], as a source for tungsten. Cobalt sulfate was used as a source for the cobalt ions and sodium hypophosphite as the reducing agent and a source for phosphorus. The Co(W, P) thin films from solutions with tungsten phosphoric acid were studied and compared to Co(W, P) films that had been obtained from solutions wherein the tungsten was supplied by tungstate ions. The use of tungsten phosphoric acid allowed higher tungsten content and lower deposition rate when compared to solutions with Na2WO4 and (NH4)(2)WO4. The deposition with tungsten phosphoric acid was studied for 20-200 nm thick layers and was found to ire reproducible. The deposited layers were bright colored and their specific resistance was in the rang of 48-90 mu Ohm cm. The process parameters of typical solutions are presented and discussed. The film sheer resistance, composition, and surface morphology are presented for various solutions and process conditions. The deposition process involves several reactions that occur simultaneously and are described in this work. Finally, various applications are proposed for copper metallization as a barrier layer, to confine the copper, or as a capping layer to prevent copper oxidation and improve adhesion of the inlaid copper to upper interlevel dielectric layers. (C) 2001 The Electrochemical Society. All rights reserved.
引用
收藏
页码:C162 / C167
页数:6
相关论文
共 22 条
[1]  
BABADZAHARJAN AA, 1963, RUSS J STRUCT CHEM, V4, P346
[2]  
DIXIT G, 1998, P ADV MET C AMC 1998, P289
[3]   Selective and blanket electroless copper deposition for ultralarge scale integration [J].
Dubin, VM ;
ShachamDiamand, Y ;
Zhao, B ;
Vasudev, PK ;
Ting, CH .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1997, 144 (03) :898-908
[4]   Full copper wiring in a sub-0.25 μm CMOS ULSI technology [J].
Edelstein, D ;
Heidenreich, J ;
Goldblatt, R ;
Cote, W ;
Uzoh, C ;
Lustig, N ;
Roper, P ;
McDevitt, T ;
Motsiff, W ;
Simon, A ;
Dukovic, J ;
Wachnik, R ;
Rathore, H ;
Schulz, R ;
Su, L ;
Luce, S ;
Slattery, J .
INTERNATIONAL ELECTRON DEVICES MEETING - 1997, TECHNICAL DIGEST, 1997, :773-776
[5]  
GORBUNOVA KM, 1974, PHYSICAL CHEM ORIGIN
[6]   Diffusion barrier properties of TaC between Si and Cu [J].
Imahori, J ;
Oku, T ;
Murakami, M .
THIN SOLID FILMS, 1997, 301 (1-2) :142-148
[7]  
INNI T, 1958, J MET FINISH SOC JPN, V9, P288
[8]  
KEUNE H, 1972, CHIMICA WISSENSSPEIC, P171
[9]  
KIKKAWA T, 1998, P ADV MET C AMC MAT
[10]  
LOPATIN S, 1996, P FALL MAT RES SOC M, V451, P463