Processing of nanostructured WC-Co powder from precursor obtained by co-precipitation

被引：69

作者：

Zhang, ZY ^{[1
]}

Wahlberg, S ^{[1
]}

Wang, MS ^{[1
]}

Muhammed, M ^{[1
]}

机构：

[1] Royal Inst Technol, Dept Mat Sci & Engn, Mat Chem Div, SE-10044 Stockholm, Sweden

来源：

NANOSTRUCTURED MATERIALS | 1999年 / 12卷 / 1-4期

关键词：

D O I：

10.1016/S0965-9773(99)00089-6

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The paper reports the processing of a homogenous cobalt tungstate salt synthesised by co-precipitation starting from ammonium paratungstate and cobalt hydroxide. Different processing parameters such as temperatures and times of reduction and carburization and the composition of the carburization gas were studied. Powders of W and Co were obtained after the reduction of the precursor at 600 'C, 650 'C and 700 'C. The specific surface area of W-Co powders increased with decreasing reduction temperature. The carburization was carried out at 700 'C for 3 hours in different CO/CO2 - mixtures. The extent of the reaction was found to depend on the CO/CO2 - ratio. A nanophase WC-Co powder agglomerated at the micrometer scale was obtained after carburization in a 90%CO/10%CO2 gas-mixture. (C) 1999 Acta Metallurgica Inc.

引用

页码：163 / 166

页数：4

共 6 条

[1] Chemical processing and properties of nanostructured WC-Co materials [J].

Kear, B.H. ;

McCandlish, L.E. .

Nanostructured Materials, 1993, 3 (1-6)

[2]

Muhammed M., 1997, U. S. Patent, Patent No. [5 594 929, 5594929]

[3]

SEEGOPAUL P, 1996, METAL POWDER REP APR, V16

[4] Nanostructured hard material composites by molecular engineering .1. Synthesis from soluble tungstate salts [J].

Wahlberg, S ;

Grenthe, I ;

Muhammed, M .

NANOSTRUCTURED MATERIALS, 1997, 9 (1-8) :105-108

[5]

WAHLBERG S, UNPUB

[6]

YAO Z, 1998, METAL POWDER REP MAR, P26

← 1 →