Effect of BaO ratio on the structure of glass-ceramic composite materials from the SiO2-Al2O3-Na2O-K2O-CaO system

This article focused on effect of the content of barium oxide on microstructure of the glass ceramic materials based on the system SiO2-Al2O3-Na2O-K2O-CaO. The following characterisation techniques have been used: X-ray diffraction (XRD), scanning electron microscopy with micro-analyser (SEM-EDS), mid-infrared analysis (Mm), far-infrared analysis (FIR) and Raman Spectroscopy. Significant differences were observed in microstructure of silica alumina network of glassy phase and phase composition related to changes in the amount of the barium oxide additive. Discussed results are part of a larger project implemented under the PBS Applied Research Programme, in order to determine the compositions of glass ceramic materials with potential application as a chemically resistant hard coatings or/and resistant to thermal shock or as construction materials. (C) 2015 Elsevier Ltd and Techna Group S.r.l. All rights reserved.