Hot Deformation and Dynamic Recrystallization of 17-4 PH Stainless Steel

被引:82
作者
Mirzadeh, Hamed [1 ]
Najafizadef, Abbas [2 ]
机构
[1] Univ Tehran, Coll Engn, Sch Met & Mat Engn, Tehran, Iran
[2] Isfahan Univ Technol, Dept Mat Engn, Esfahan 8415683111, Iran
关键词
hot deformation; dynamic recrystallization; grain refining; DRX map; AUSTENITE GRAIN-SIZE; METADYNAMIC RECRYSTALLIZATION; MICROSTRUCTURAL EVOLUTION; FLOW-STRESS; STRAIN-RATE; WORKING; NB; MECHANISMS; INITIATION; BEHAVIOR;
D O I
10.2355/isijinternational.53.680
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
The hot deformation behavior of a 17-4 PH stainless steel was investigated by compression tests. The typical single-peak dynamic recrystalization (DRX) behavior and also a transition state between single and multiple peak (cyclic) behaviors were seen in the resultant flow curves. The application of constitutive equations for determination of hot working constants was critically discussed. As a result, the deformation activation energy and the stress multiplier in the hyperbolic sine equation were determined as 337 kJ/mol and 0.011, respectively. The Zener-Hollomon parameter (Z) exponents for peak stress and peak strain based on the power relationships were determined as 0.18 and 0.11, respectively. The normalized critical stress and strain for initiation of DRX were respectively found to be 0.89 and 0.47. The prior austenite grain boundaries (PAGB) were revealed by electrolytic etching of the martensite in order to study the microstructure of hot deformed samples. Significant grain refinement occurred as a result of necklace DRX mechanism. The average dynamically recrystallized grain size was related to Z and peak stress by power equations with exponents of -0.25 and -1.24, respectively. A DRX map was developed to show the effect of deformation conditions on the occurrence of DRX and on the final grain size.
引用
收藏
页码:680 / 689
页数:10
相关论文
共 65 条
[1]  
Ashby M.F., 1982, DEFORMATION MECH MAP
[2]  
ASM, 1985, MET HDB, V9
[3]   Dynamic recrystallization under warm deformation of a 304 type austenitic stainless steel [J].
Belyakov, A ;
Miura, H ;
Sakai, T .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1998, 255 (1-2) :139-147
[4]   ETCHING AND IMAGE-ANALYSIS OF PRIOR AUSTENITE GRAIN-BOUNDARIES IN HARDENED STEELS [J].
BREWER, AW ;
ERVEN, KA ;
KRAUSS, G .
MATERIALS CHARACTERIZATION, 1991, 27 (01) :53-56
[5]   The dynamic, static and metadynamic recrystallization of a Nb-microalloyed steel [J].
Cho, SH ;
Kang, KB ;
Jonas, JJ .
ISIJ INTERNATIONAL, 2001, 41 (01) :63-69
[6]   Hot rolling simulations of austenitic stainless steel [J].
Cho, SH ;
Yoo, YC .
JOURNAL OF MATERIALS SCIENCE, 2001, 36 (17) :4267-4272
[7]   Metallographic techniques for the determination of the austenite grain size in medium-carbon microalloyed steels [J].
de Andrés, CG ;
Bartolomé, MJ ;
Capdevila, C ;
Martín, DS ;
Caballero, FG ;
López, V .
MATERIALS CHARACTERIZATION, 2001, 46 (05) :389-398
[8]   Hot deformation and recrystallization of austenitic stainless steel: Part I. Dynamic recrystallization [J].
Dehghan-Manshadi, A. ;
Barnett, Mr. ;
Hodgson, P. D. .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2008, 39A (06) :1359-1370
[9]   THE DEPENDENCE OF GRAIN-SIZE ON STRESS DURING DYNAMIC RECRYSTALLIZATION [J].
DERBY, B .
ACTA METALLURGICA ET MATERIALIA, 1991, 39 (05) :955-962
[10]   Current issues in recrystallization: a review [J].
Doherty, RD ;
Hughes, DA ;
Humphreys, FJ ;
Jonas, JJ ;
Jensen, DJ ;
Kassner, ME ;
King, WE ;
McNelley, TR ;
McQueen, HJ ;
Rollett, AD .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1997, 238 (02) :219-274