Analysis of Microstructure and Micro Mechanical Properties for Weld Joints of 1000MPa Class Steel by Nanoindentation Technique

被引：1

作者：

Peng, Xingna ^{[1
]}

Peng, Yun ^{[1
]}

Wei, Jinshan ^{[1
]}

Tian, Zhiling ^{[1
]}

机构：

[1] Cent Iron & Steel Res Inst, State Key Lab Adv Steel Proc & Prod, Beijing 100081, Peoples R China

来源：

ADVANCED MATERIALS AND PROCESS TECHNOLOGY, PTS 1-3 | 2012年 / 217-219卷

关键词：

HSLA steel; nanoindentation; hardness; weld; microstructure; CONTINUOUS STIFFNESS MEASUREMENT; INSTRUMENTED INDENTATION; ELASTIC-MODULUS; HARDNESS; BEHAVIOR;

D O I：

10.4028/www.scientific.net/AMM.217-219.1987

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Nanoindentation technique was employed to examine the nanohardness and elastic modulus of weld joints of 1000MPa Class high strength low alloy (HSLA) steel. The distribution of micro scales mechanical behavior was analyzed combined with microstructure observation by OM, SEM and TEM. It was shown that weld metal and base metal were mainly of bainite and their nanohardness is about 4.0GPa. In the heat affected zone, fine grained heat affected zone and coarse grained heat affected zone with lath martensite structure had the maximum hardness (above 4.75GPa). From inter critical region, the hardness of HAZ decreased to 2.5 GPa. However, the elastic modulus of metallic material is not much sensitive to the microstructure.

引用

页码：1987 / 1993

页数：7

共 11 条

[1]

Chen Shujun, 2010, T JWRI, V39, P229

[2] Analysis of mechanical property distribution in multiphase ultra-fine-grained steels by nanoindentation [J].

Choi, Y ;

Choo, WY ;

Kwon, D .

SCRIPTA MATERIALIA, 2001, 45 (12) :1401-1406

[3] Assessing welding residual stress in A335 P12 steel welds before and after stress-relaxation annealing through instrumented indentation technique [J].

Jang, JI ;

Son, D ;

Lee, YH ;

Choi, Y ;

Kwon, D .

SCRIPTA MATERIALIA, 2003, 48 (06) :743-748

[4]

Li XD, 2002, MATER CHARACT, V48, P11, DOI 10.1016/S1044-5803(02)00192-4

[5] Continuous stiffness measurement and creep behavior of composite magnetic tapes [J].

Li, XD ;

Bhushan, B .

THIN SOLID FILMS, 2000, 377 :401-406

[6] Application of nanoindentation technique for structural characterisation of weld materials [J].

Maier, P ;

Richter, A ;

Faulkner, RG ;

Ries, R .

MATERIALS CHARACTERIZATION, 2002, 48 (04) :329-339

[7] Effect of thermo-mechanical cycling on the microstructure and strength of lath martensite in the weld CGHAZ of HSLA steel [J].

Moon, Joonoh ;

Kim, Seong-Ju ;

Lee, Changhee .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2011, 528 (25-26) :7658-7662

[8] Evaluation of temper softening behavior of Fe-C binary martensitic steels by nanoindentation [J].

Ohmura, T ;

Hara, T ;

Tsuzaki, K .

SCRIPTA MATERIALIA, 2003, 49 (12) :1157-1162

[9] Measurement of hardness and elastic modulus by instrumented indentation: Advances in understanding and refinements to methodology [J].

Oliver, WC ;

Pharr, GM .

JOURNAL OF MATERIALS RESEARCH, 2004, 19 (01) :3-20

[10] AN IMPROVED TECHNIQUE FOR DETERMINING HARDNESS AND ELASTIC-MODULUS USING LOAD AND DISPLACEMENT SENSING INDENTATION EXPERIMENTS [J].

OLIVER, WC ;

PHARR, GM .

JOURNAL OF MATERIALS RESEARCH, 1992, 7 (06) :1564-1583

← 1 2 →