Microstructures and properties of TiN reinforced Co-based composite coatings modified with Y2O3 by laser cladding on Ti-6Al-4V alloy

被引：97
作者：
Weng, Fei [1 ,3 ]
Yu, Huijun [2 ,3 ]
Chen, Chuanzhong [1 ,3 ]
Liu, Jianli [1 ,3 ]
Zhao, Longjie [1 ,3 ]
机构：
[1] Shandong Univ, Dept Mat Sci & Engn, Minist Educ, Key Lab Liquid Solid Struct Evolut & Proc Mat, Jinan 250061, Peoples R China
[2] Shandong Univ, Sch Mech Engn, Minist Educ, Key Lab High Efficiency & Clean Mech Manufacture, Jinan 250061, Peoples R China
[3] Shandong Univ, Suzhou Inst, Suzhou 215123, Peoples R China
来源：
JOURNAL OF ALLOYS AND COMPOUNDS | 2015年 / 650卷
关键词：
Laser cladding; Titanium alloy; Composite coating; Microstructure; DRY SLIDING WEAR; MECHANICAL-PROPERTIES; TITANIUM; RESISTANCE; WC; PERFORMANCE; IMPROVEMENT; EVOLUTION; CORROSION; NANO-Y2O3;
D O I：
10.1016/j.jallcom.2015.07.295
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
In this study, TiN reinforced composite coatings were fabricated on Ti-6Al-4V substrate by laser cladding with Co42 self-fluxing alloy, TiN and Y2O3 mixed powders. Microstructures and wear resistance of the cladding coatings with and without Y2O3 addition were investigated comparatively. Results showed that the coatings were mainly comprised of g-Co/Ni, TiN, CoTi, CoTi2, NiTi, TiC, Cr7C3, TiB, Ti5Si3 and TiC0.3N0.7 phases. The coatings showed metallurgical bonding free of pores and cracks with the substrate. Compared with the Ti-6Al-4V substrate, the microhardness and wear resistance of the coatings was enhanced by 3-4 times and 9.5-11.9 times, respectively. With 1.0 wt.% Y2O3 addition, the microstructure of the coating was refined significantly, and the microhardness and dry sliding wear resistance were enhanced further. The effects of Y2O3 were attributed to the residual Y2O3 and decomposed Y atoms. (C) 2015 Elsevier B.V. All rights reserved.
引用
收藏
页码：178 / 184
页数：7
相关论文
共 40 条
[1]   Laser cladding assisted by induction heating of Ni-WC composite enhanced by nano-WC and La2O3 [J].
Farahmand, Parisa ;
Liu, Shuang ;
Zhang, Zhe ;
Kovacevic, Radovan .
CERAMICS INTERNATIONAL, 2014, 40 (10) :15421-15438
[2]   Cladding of pre-blended Ti-6Al-4V and WC powder for wear resistant applications [J].
Farayibi, P. K. ;
Folkes, J. ;
Clare, A. ;
Oyelola, O. .
SURFACE & COATINGS TECHNOLOGY, 2011, 206 (2-3) :372-377
[3]   Effect of actual WC content on the reciprocating wear of a laser cladding NiCrBSi alloy reinforced with WC [J].
Fernandez, M. R. ;
Garcia, A. ;
Cuetos, J. M. ;
Gonzalez, R. ;
Noriega, A. ;
Cadenas, M. .
WEAR, 2015, 324 :80-89
[4]   Microstructure and wear resistance of one-step in-situ synthesized TiN/Al composite coatings on Ti6Al4V alloy by a laser nitriding process [J].
Fu, Yao ;
Zhang, Xian-Cheng ;
Sui, Jian-Feng ;
Tu, Shan-Tung ;
Xuan, Fu-Zhen ;
Wang, Zheng-Dong .
OPTICS AND LASER TECHNOLOGY, 2015, 67 :78-85
[5]   Effect of TiNi in dry sliding wear of laser melt deposited Ti2Ni/TiNi alloys [J].
Gao, F. ;
Wang, H. M. .
MATERIALS CHARACTERIZATION, 2008, 59 (09) :1349-1354
[6]   Dry sliding wear property of a laser melting/deposited Ti2Ni/TiNi intermetallic alloy [J].
Gao, F. ;
Wang, H. M. .
INTERMETALLICS, 2008, 16 (02) :202-208
[7]   Microstructure and wear behavior of stellite 6 cladding on 17-4 PH stainless steel [J].
Gholipour, A. ;
Shamanian, M. ;
Ashrafizadeh, F. .
JOURNAL OF ALLOYS AND COMPOUNDS, 2011, 509 (14) :4905-4909
[8]   Creep mechanisms in particle strengthened α-titanium-Ti2Co alloys [J].
Hofmann, H ;
Frommeyer, G ;
Derder, C .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1998, 245 (01) :127-134
[9]   Corrosion and mechanical-micro structural aspects of dissimilar joints of Ti-6Al-4V and Al plates [J].
Kahraman, Nizamettin ;
Gulenc, Behcet ;
Findik, Fehim .
INTERNATIONAL JOURNAL OF IMPACT ENGINEERING, 2007, 34 (08) :1423-1432
[10]   Large-area high-rate pulsed laser deposition of smooth TiCxN1-x coatings at room temperature-mechanical and tribological properties [J].
Lackner, JM ;
Waldhauser, W ;
Ebner, R .
SURFACE & COATINGS TECHNOLOGY, 2004, 188 :519-524
1234