Effect of plasma electrolytic oxidation coating on the stress corrosion cracking behaviour of wrought AZ61 magnesium alloy

被引：47
|
作者：
Srinivasan, P. Bala [1 ]
Blawert, C. [1 ]
Dietzel, W. [1 ]
机构：
[1] GKSS Forschungszentrum Geesthacht GmbH, Inst Mat Res, D-21502 Geesthacht, Germany
来源：
CORROSION SCIENCE | 2008年 / 50卷 / 08期
关键词：
Magnesium; SEM; Anodic films; Stress corrosion;
D O I：
10.1016/j.corsci.2008.05.018
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
An attempt was made to understand the effect of silicate based plasma electrolytic oxidation (PEO) coating on the stress corrosion cracking (SCC) behaviour of an AZ61 wrought magnesium alloy. The SCC behaviour of untreated and PEO coated specimens was assessed using slow strain rate tensile tests at two different nominal strain rates, viz. 1 x 10(-6) s(-1) and 1 X 10(-7) s(-1). in ASTM D1384 test solution at ambient conditions. The PEO coating was found to improve the general corrosion resistance to a significant extent: however, the improvement in the resistance to stress corrosion cracking was only marginal. (C) 2008 Elsevier Ltd. All rights reserved.
引用
收藏
页码：2415 / 2418
页数：4
相关论文
共 50 条
  • [41] Corrosion resistance of plasma electrolytic oxidation layer of a non-ignitable Mg-Al-Mn-Ca magnesium alloy
    Mori, Yoichi
    Koshi, Akihiko
    Liao, Jinsun
    CORROSION SCIENCE, 2016, 104 : 207 - 216
  • [42] The effect of low temperature heat treatment on surface chemistry and corrosion resistance of commercial magnesium alloys AZ31 and AZ61 in 0.6 M NaCl solution
    Feliu, Sebastian, Jr.
    Samaniego, Alejandro
    Barranco, Violeta
    El-Hadad, A. A.
    Llorente, Irene
    Adeva, P.
    CORROSION SCIENCE, 2014, 80 : 461 - 472
  • [43] Electrolytic MgO/ZrO2 duplex-layer coating on AZ91D magnesium alloy for corrosion resistance
    Wang, Ming-Jia
    Li, Ching-Fei
    Yen, Shiow-Kang
    CORROSION SCIENCE, 2013, 76 : 142 - 153
  • [44] GALVANIC CORROSION AND STRESS CORROSION CRACKING OF STEEL AND ALUMINUM BOLTS IN MAGNESIUM DIE CAST ALLOY AZ91
    Gerstmayr, Gerhard
    Mori, Gregor
    Eichlseder, Wilfried
    MAGNESIUM TECHNOLOGY 2010, 2010, : 145 - +
  • [45] Effect of Na2SiF6 concentration on the plasma electrolytic oxidation of AZ31B magnesium alloy
    Rehman, Zeeshan Ur
    Ahn, Byung Hyun
    Song, Jung Il
    Koo, Bon Heun
    INTERNATIONAL JOURNAL OF SURFACE SCIENCE AND ENGINEERING, 2016, 10 (05) : 456 - 467
  • [46] Characteristics and corrosion resistance of plasma electrolytic oxidation coatings on AZ31B Mg alloy formed in phosphate - Silicate mixture electrolytes
    Mori, Yoichi
    Koshi, Akihiko
    Liao, Jinsun
    Asoh, Hidetaka
    Ono, Sachiko
    CORROSION SCIENCE, 2014, 88 : 254 - 262
  • [47] Effect of Starch Addition in Alkaline Electrolyte on the Characteristics of Plasma Electrolytic Oxidation Coating on AZ31B Mg Alloy
    Fang, Yinyu
    Tu, Xiaohua
    Miao, Chengping
    Xu, Yaling
    Xie, Wei
    Chen, Fangda
    Zhang, Yang
    Li, Jiayou
    INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2017, 12 (12): : 11473 - 11478
  • [48] Structure-property quantification of corrosion pitting under immersion and salt-spray environments on an extruded AZ61 magnesium alloy
    Martin, Holly J.
    Horstemeyer, M. F.
    Wang, Paul T.
    CORROSION SCIENCE, 2011, 53 (04) : 1348 - 1361
  • [49] Effect of Oxidation and Hot Corrosion on Stress Corrosion Cracking Susceptibility of Inconel 738 Alloy
    Patil, A. R.
    Vagge, S. T.
    STRENGTH OF MATERIALS, 2023, 55 (03) : 582 - 605
  • [50] Effect of Oxidation and Hot Corrosion on Stress Corrosion Cracking Susceptibility of Inconel 738 Alloy
    A. R. Patil
    S. T. Vagge
    Strength of Materials, 2023, 55 : 582 - 605
12345