Effect of iron doping on SO2 and H2O resistance of honeycomb cordierite-based Mn-Ce/Al2O3 catalyst for NO removal at low temperature

被引：17
作者：
Wang, Cheng-zhi [1 ]
Zhao, Yong-gang [1 ]
Zhang, Cheng [1 ]
Yan, Xin [2 ]
Cao, Peng [1 ]
机构：
[1] Shihezi Univ, Key Lab Green Proc Chem Engn Xinjiang Bingtuan, Sch Chem & Chem Engn, Shihezi 832003, Xinjiang, Peoples R China
[2] Tianfu South Thermoelect Co Ltd, Shihezi 832000, Xinjiang, Peoples R China
来源：
RESEARCH ON CHEMICAL INTERMEDIATES | 2018年 / 44卷 / 05期
基金：
国家高技术研究发展计划(863计划);
关键词：
Low-temperature selective catalytic reduction; SO2; resistance; Honeycomb cordierite; Mn-Ce/Al2O3; catalyst; Fe doping; SULFUR-RESISTANCE; MANGANESE OXIDES; SOLID-SOLUTIONS; SCR CATALYSTS; REDUCTION; NH3; PERFORMANCE; SURFACE; MECHANISM; OXIDATION;
D O I：
10.1007/s11164-018-3297-0
中图分类号：
O6 [化学];
学科分类号：
0703 ;
摘要：
Honeycomb cordierite-based Mn-Ce/Al2O3 (Mn-Ce/Al2O3-C) and Fe-Mn-Ce/Al2O3 (Fe-Mn-Ce/Al2O3-C) catalysts were prepared by an impregnation method and investigated in low-temperature selective catalytic reduction (SCR) of NO with NH3 at 100 A degrees C. The Fe-Mn-Ce/Al2O3-C catalyst exhibited not only higher catalytic activity, but also much better SO2 and H2O resistance in the presence of 30 ppm SO2 and/or 5 vol% H2O than Mn-Ce/Al2O3-C. After doping Fe, the NO conversion of Mn-Ce/Al2O3-C catalyst displayed an increasing trend from 79 to 84% in the absence of SO2 and H2O at 100 A degrees C under a gas hour space velocity of 1667 h(-1). The results of characterization indicated that addition of Fe was advantageous to increase BET surface area, pore volume and inhibit loss of surface Mn and Ce species. Additionally, it was helpful for generating higher concentration of Mn4+, more chemisorbed oxygen and more uniform dispersion of amorphous Mn and Ce in the surface of catalyst, which were beneficial to interact with reactants. Furthermore, in contrast to Mn-Ce/Al2O3-C, the SCR activity of Fe-Mn-Ce/Al2O3-C catalyst in the presence of H2O, SO2 and H2O and SO2 were 79, 75 and 64%, with the increase of 14, 18 and 19%, respectively. It is indicated that the addition of Fe could inhibit sulfate formation and thus enhance SO2 resistance. XPS results reveal that the doping of Fe into the ceria lattice led to some Ce4+ transferred into Ce3+ in order to maintain the electrical neutrality, thereby facilitating the reduction of Ce4+ -> Ce3+ and the formation of oxygen vacancies. NH3 temperature-programmed desorption (TPD) results imply that the doping of Fe onto Mn-Ce/Al2O3-C can remarkably improve the distribution and concentration of acid sites. All the above factors contributed to the improvement of overall NH3 SCR performance of the Fe-Mn-Ce/Al2O3-C catalyst compared with that of the Mn-Ce/Al2O3-C catalyst.
引用
收藏
页码：3135 / 3150
页数：16
相关论文
共 50 条
[21]   Characterization and reactivity of V2O5-MoO3/TiO2 De-NOx SCR catalysts [J].
Lietti, L ;
Nova, I ;
Ramis, G ;
Dall'Acqua, L ;
Busca, G ;
Giamello, E ;
Forzatti, P ;
Bregani, F .
JOURNAL OF CATALYSIS, 1999, 187 (02) :419-435
[22]  
Liu F., 2009, APPL CATAL B-ENVIRON, V93, P3760
[23]   Selective catalytic reduction of NOx by NH3 over MoO3-promoted CeO2/TiO2 catalyst [J].
Liu, Zhiming ;
Zhu, Junzhi ;
Zhang, Shaoxuan ;
Ma, Lingling ;
Woo, Seong Ihl .
CATALYSIS COMMUNICATIONS, 2014, 46 :90-93
[24]   SO2 Deactivation Mechanism of MnOx/MWCNTs Catalyst for Low-Temperature Selective Catalytic Reduction of NOx by Ammonia [J].
Luo Hong-Cheng ;
Huang Bi-Chun ;
Fu Ming-Li ;
Wu Jun-Liang ;
Ye Dai-Qi .
ACTA PHYSICO-CHIMICA SINICA, 2012, 28 (09) :2175-2182
[25]   Catalytic reduction of NO by NH3 over Fe-Cu-OX/CNTs-TiO2 composites at low temperature [J].
Ma, Zhaoxia ;
Yang, Hangsheng ;
Li, Qian ;
Zheng, Junwei ;
Zhang, Xiaobin .
APPLIED CATALYSIS A-GENERAL, 2012, 427 :43-48
[26]   CO and soot oxidation activity of doped ceria: Influence of dopants [J].
Mukherjee, Deboshree ;
Rao, Bolla Govinda ;
Reddy, Benjaram M. .
APPLIED CATALYSIS B-ENVIRONMENTAL, 2016, 197 :105-115
[27]   Nature of manganese species in Ce1-xMnxO2-δ solid solutions synthesized by the solution combustion route [J].
Murugan, B ;
Ramaswamy, AV ;
Srinivas, D ;
Gopinath, CS ;
Ramaswamy, V .
CHEMISTRY OF MATERIALS, 2005, 17 (15) :3983-3993
[28]   Characterization of corrosion products formed on the surface of carbon steel by Raman spectroscopy [J].
Nie, Xianghui ;
Li, Xiaogang ;
Du, Cuiwei ;
Huang, Yizhong ;
Du, He .
JOURNAL OF RAMAN SPECTROSCOPY, 2009, 40 (01) :76-79
[29]   Identification of surface species on titania-supported manganese, chromium, and copper oxide low-temperature SCR catalysts [J].
Peña, DA ;
Uphade, BS ;
Reddy, EP ;
Smirniotis, PG .
JOURNAL OF PHYSICAL CHEMISTRY B, 2004, 108 (28) :9927-9936
[30]   TiO2-supported metal oxide catalysts for low-temperature selective catalytic reduction of NO with NH3I.: Evaluation and characterization of first row transition metals [J].
Peña, DA ;
Uphade, BS ;
Smirniotis, PG .
JOURNAL OF CATALYSIS, 2004, 221 (02) :421-431
12345