Prospects for laser-ultrasonic treatment for surface modification, welding, and pattern cutting

Heat and mass transport, structurization, and residual-stress formation in the course of laser-ultrasonic hardening, near-surface alloying, rapid crystallization of melts, and pattern cutting are experimentally studied with allowance made for the theoretical concept that ultrasound influences the processes of phase transformations and diffusion under conditions of high-rate laser heating and subsequent cooling. It is shown that harder and deeper hardening zones and melt baths are formed under the laser-ultrasonic treatment. plastic deformation of the surface by ultrasound significantly affects the completeness of austenitic transformation and thus makes it possible to efficiently control the strained state of the surface in the zone exposed to laser radiation. Acoustic hows emerging in the laser-induced melt smooth the temperature nonuniformities and the topography of the melt surface efficiently even when the duration of the laser exposure is about 1 ms. The influence of the geometry of injecting the ultrasound on the structurization and formation of residual stresses during rapid crystallization of the laser-induced melt and the subsequent tempering was observed. It was established that the injection of ultrasound into the laser-induced melt brings about a more efficient alloying and better micromechanical characteristics of the surface. The laser-ultrasonic pattern cutting of metal without the formation of flashes was realized.