Characterization of Cr-α-Al2O3 Composite Coatings Electrodeposited from Cr(III) Plating Bath

被引：0
|
作者：
Sun, Xin [1 ]
He, Xiangzhu [1 ]
Wang, Yongxiu [1 ]
Fu, Zhihong [1 ]
机构：
[1] Guangdong Univ Technol, Fac Chem Engn & Light Ind, Guangzhou 510006, Guangdong, Peoples R China
来源：
FRONTIERS OF MANUFACTURING AND DESIGN SCIENCE II, PTS 1-6 | 2012年 / 121-126卷
关键词：
Cr-alpha-Al2O3; composite coating; trivalent chromium; corrosion resistance; CHROMIUM DEPOSITS; BEHAVIOR; RESISTANCE; CORROSION; ALLOYS;
D O I：
10.4028/www.scientific.net/AMM.121-126.60
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Cr-alpha-Al2O3 composite coatings were prepared by direct current deposition experiments from Cr(III) plating bath and the thickness of composite coatings could be up to 14 mu m. The obtained Cr-alpha-Al2O3 coatings and Cr coatings were characterized by means of EDS, SEM and microhardness measurement. Results revealed that Cr-alpha-Al2O3 coatings exhibit fine-grained structure with uniform surface and the highest microhardness values(692 HV) when the alpha-Al2O3 content of coatings was 15g/L, although some pores and defects are still present in the coatings. Analysis of Tafel curves indicated that the presence of alpha-Al2O3 in the Cr coatings show better features in the corrosion resistance both in H2SO4 and NaOH solution than those prepared from the bath without alpha-Al2O3.
引用
收藏
页码：60 / 64
页数：5
相关论文
共 50 条
  • [21] Corrosion and tribological behavior of Ni-Cr alloy coatings electrodeposited on low carbon steel in Cr (III)-Ni (II) bath
    Aghdam, A. Sheibani
    Allahkaram, S. R.
    Mahdavi, S.
    SURFACE & COATINGS TECHNOLOGY, 2015, 281 : 144 - 149
  • [22] First-principles calculation of oxygen absorption, solution and diffusion in Zr and its coatings (Cr, Cr/α-Al2O3)
    Yang, Yiying
    Zhou, Xiaokai
    Li, Rongchuan
    Xin, Tianyuan
    Si, Jiaxuan
    Li, Yaojun
    Wang, Yuexia
    JOURNAL OF NUCLEAR MATERIALS, 2025, 609
  • [23] Comprehensive study on corrosion protection properties of Al2O3, Cr2O3 and Al2O3-Cr2O3 ceramic coatings deposited by plasma spraying on carbon steel
    Zamani, Pejman
    Valefi, Zia
    Jafarzadeh, Kourosh
    CERAMICS INTERNATIONAL, 2022, 48 (02) : 1574 - 1588
  • [24] Microstructures and mechanical properties of (Ti,Cr)Al/Al2O3 composites fabricated by reactive hot pressing from Ti, Al and Cr2O3
    Zhu, Jianfeng
    Yang, Wenwen
    Wang, Fen
    JOURNAL OF ALLOYS AND COMPOUNDS, 2013, 567 : 15 - 20
  • [25] A Dense Cr2O3/Al2O3 Composite Ceramic Coating Prepared by Electrodeposition and Sealing with Al2O3
    Di, Jiao
    Liu, Wei
    Xue, Lihong
    Zhou, Qilai
    Yan, Youwei
    COATINGS, 2019, 9 (01):
  • [26] Synthesis and characterization of electrodeposited Ni-B-Tl2O3 composite coatings
    Waware, Umesh Somaji
    Hamouda, A. M. S.
    Bajaj, Bharat
    Borkar, Tushar
    Pradhan, A. K.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2018, 769 : 353 - 359
  • [27] The microstructure and hardness properties of plasma sprayed Cr2O3/Al2O3 coatings
    Ozel, S.
    Vural, E.
    JOURNAL OF OPTOELECTRONICS AND ADVANCED MATERIALS, 2016, 18 (11-12): : 1052 - 1056
  • [28] Influence of Cr content and initial Cr particle size on the dielectric properties of plasma-sprayed Cr/Al2O3 coatings
    Zhou, Liang
    Dong, Yanli
    Wang, Zhenjun
    Wang, Yuxin
    Hua, Dongpeng
    SURFACE & COATINGS TECHNOLOGY, 2017, 313 : 374 - 380
  • [29] Composite Ni/Al2O3 coatings and their corrosion resistance
    Szczygiel, B
    Kolodziej, M
    ELECTROCHIMICA ACTA, 2005, 50 (20) : 4188 - 4195
  • [30] Characteristics and corrosion behavior of as-deposited and heat-treated Co-Cr/ZrO2 coatings electrodeposited from Cr(III) baths
    Mahmoudi, E.
    Mohitfar, S. H.
    Mahdavi, S.
    MATERIALS CHEMISTRY AND PHYSICS, 2021, 272
12345