The influence of Ni-rich nanoclusters on the anisotropic magnetic properties of CdSb doped with Ni

The magnetic properties of oriented CdSb single crystals doped with 2 at% of Ni are investigated. From measurements of magnetic irreversibility defined by deviation of the zero-field-cooled (ZFC) susceptibility from the field-cooled (FC) susceptibility, the value of the mean anisotropy field B-K similar to 4 kG is obtained. The ZFC susceptibility displays a broad maximum at a blocking temperature, T-b, depending on B according to the law [T-b(B)/T-b(0)](1/2) = 1 - B/B-K with T-b(0) similar to 100 K. The field dependence of the magnetization exhibits saturation above similar to 20-30 kG with values of M-s different for B along the [10 0], [0 10] and [0 0 11 axes. The temperature dependence of M, is weak, increasing slightly upon cooling the sample below similar to 100 K. The temperature dependence of the coercive field, B, (T), is weak above Tb but is enhanced strongly with decreasing temperature below Tb. The anisotropy of B, is inverted with respect to the anisotropy of Ms. Such behaviour can be attributed to spheroidal Ni-rich Ni1-xSbx nanoparticles with a high aspect ratio, broad size distribution and distribution of the orientation of the major axis around a preferred direction. The relation B-c << B-K and the anisotropies of M-s and B-c are consistent with reversal of the magnetization by the curling mode, whereas the Tb(B) dependence is typical of the coherent rotation mode. This difference is connected to the proximity of the average transversal cluster radius to a critical value for transition between the two magnetization reversal modes within a wide crossover interval, due to broad distribution of the cluster sizes.