Precipitation during homogenization cooling in AlMgSi alloys

被引：24

作者：

Birol, Yucel ^{[1
]}

机构：

[1] TUBITAK, Mat Inst, Marmara Res Ctr, TR-41470 Kocaeli, Turkey

来源：

TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA | 2013年 / 23卷 / 07期

关键词：

aluminium alloys; extrusion; precipitation; homogenization; MG-SI ALLOYS; MICROSTRUCTURE CONTROL; ALUMINUM-ALLOY; SEQUENCE; PHASES;

D O I：

10.1016/S1003-6326(13)62672-2

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Precipitation during the industrial cool down takes place predominantly above 300 degrees C in the EN AW-6082 and 6005 alloys. The phase precipitation throughout cooling is equilibrium beta phase. A considerable capacity is retained after the cool down for further precipitation during a subsequent heating cycle. The beta-Mg2Si is once again the predominant phase that forms during a scan heating cycle employed in exactly the same manner with the industrial billet preheating operation. The precipitation in the 6060 alloy, on the other hand, occurs predominantly below 300 degrees C with additionally beta'-Mg2Si particles formed below 200 degrees C.

引用

页码：1875 / 1881

页数：7

共 20 条

[1]

Beatty E.C, 1969, P 1 INT AL EXTR TECH, P10

[2] The effect of processing and Mn content on the T5 and T6 properties of AA6082 profiles [J].

Birol, Y .

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2006, 173 (01) :84-91

[3]

Birol Y, 2004, J MATER PROCESS TECH, V148, P250, DOI [10.1016/j.jmatprotec.2004.01.056, 10.1016/j.matprotec.2004.01.056]

[4] Calorimetric study of 6061-Al-15 vol.% SiCw PM composites extruded at different temperatures [J].

Borrego, A ;

Gonzalez-Doncel, G .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1998, 245 (01) :10-18

[5] Analysis of the intermetallic phase transformation occurring during homogenization of 6xxx aluminum alloys [J].

Claves, SR ;

Elias, DL ;

Misiolek, WZ .

ALUMINUM ALLOYS 2002: THEIR PHYSICAL AND MECHANICAL PROPERTIES PTS 1-3, 2002, 396-4 :667-674

[6] The precipitation sequence in Al-Mg-Si alloys [J].

Edwards, GA ;

Stiller, K ;

Dunlop, GL ;

Couper, MJ .

ACTA MATERIALIA, 1998, 46 (11) :3893-3904

[7] Morphology and thermal stability of Al-Mg-Si ternary alloy metastable precipitates formed in an aged at 403 K to 483 K [J].

Fukui, K ;

Takeda, M ;

Endo, T .

MATERIALS LETTERS, 2005, 59 (11) :1444-1448

[8] Precipitation hardening processes in an Al-0.40%Mg-1.3%Si-0.25%Fe aluminum alloy [J].

Gupta, AK ;

Lloyd, DJ ;

Court, SA .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2001, 301 (02) :140-146

[9] Microstructure control during extrusion with respect to surface quality [J].

Karhausen, K ;

Dons, AL ;

Aukrust, T .

ALUMINIUM ALLOYS: THEIR PHYSICAL AND MECHANICAL PROPERTIES, PTS 1-3, 1996, 217 :403-408

[10] DSC study on Mg-Si phases in as cast AA6xxx [J].

Kuijpers, NCW ;

Kool, WH ;

van der Zwaag, S .

ALUMINUM ALLOYS 2002: THEIR PHYSICAL AND MECHANICAL PROPERTIES PTS 1-3, 2002, 396-4 :675-680

← 1 2 →