Corrosion protection of NdFeB magnets by surface coatings .2. Electrochemical behaviour in various solutions

被引:35
作者
Man, HH
Man, HC
Leung, LK
机构
[1] HONG KONG POLYTECH UNIV,DEPT MFG ENGN,HONG KONG,HONG KONG
[2] HONG KONG POLYTECH UNIV,DEPT APPL PHYS,HONG KONG,HONG KONG
关键词
D O I
10.1016/0304-8853(95)00454-8
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Various surface modification techniques, including single and bimetallic electroplating, and chemical vapour deposition (CVD), have been applied to improve the poor corrosion resistance of NdFeB magnets. The corrosion resistance of the surface-treated samples has been compared with that of some commercially available coated samples including nickel, zinc, gold coatings. Potentiokinetic polarisation behaviour in 1N H2SO4, 10% H3PO4 and Ringer's solution was studied. It was found that in the 1N H2SO4 solution, the corrosion resistance of gold coating was the best, whereas in chloride-contaminated solution, Ni/Cr and gold coatings have comparable corrosion resistance. The results of salt spray tests of the coated specimens (in Part 1) were compared with the electrochemical data. In a simulated marine environment, epoxy coating was found to be slightly better than Ni/Cr coatings. Zn coating provided a certain degree of protection to the magnets in various solutions studied. The choice between cathodic, anodic and polymer coatings was found to be governed by the service environment and application.
引用
收藏
页码:47 / 53
页数:7
相关论文
共 11 条
[1]   CORROSION CHARACTERISTICS OF ND2FE14-XNIXB PERMANENT-MAGNETS [J].
BALA, H ;
SZYMURA, S ;
WYSLOCKI, JJ .
IEEE TRANSACTIONS ON MAGNETICS, 1990, 26 (05) :2646-2648
[2]   ELECTROCHEMICAL CORROSION-RESISTANCE OF FE-ND-B PERMANENT-MAGNETS [J].
BALA, H ;
SZYMURA, S ;
WYSLOCKI, JJ .
JOURNAL OF MATERIALS SCIENCE, 1990, 25 (1B) :571-574
[3]  
Croat J J, 1989, J MAGN MAGN MATER, V80, P9
[4]  
Dahm R.H., 1993, T I METAL FINISH, V71, P77, DOI DOI 10.1080/00202967.1993.11870993
[5]   OXIDATION AND OXIDATION PROTECTION OF ND-FE-B MAGNETS [J].
KIM, AS ;
JACOBSON, JM .
IEEE TRANSACTIONS ON MAGNETICS, 1987, 23 (05) :2509-2511
[6]  
MAN HH, 1994, THESIS HONG KONG POL
[7]   IMPROVEMENT OF THE CORROSION-RESISTANCE ON ND-FE-B MAGNET WITH NICKEL PLATING [J].
MINOWA, T ;
YOSHIKAWA, M ;
HONSHIMA, M .
IEEE TRANSACTIONS ON MAGNETICS, 1989, 25 (05) :3776-3778
[8]   CORROSION PROTECTION OF NDFEB MAGNETS [J].
MITCHELL, P .
IEEE TRANSACTIONS ON MAGNETICS, 1990, 26 (05) :1933-1935
[9]   STRUCTURE, MAGNETIC-PROPERTIES AND CORROSION BEHAVIOR OF SINTERED ND16FE76-XCRXB8 MAGNETS [J].
SZYMURA, S ;
BALA, H ;
RABINOVICH, YM ;
SERGEEV, VV ;
PAWLOWSKA, G .
JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 1991, 94 (1-2) :113-118
[10]   IMPROVED CORROSION AND TEMPERATURE BEHAVIOR OF MODIFIED ND-FE-B MAGNETS [J].
TENAUD, P ;
VIAL, F ;
SAGAWA, M .
IEEE TRANSACTIONS ON MAGNETICS, 1990, 26 (05) :1930-1932