In Situ Observation of the Deformation and Fracture Behaviors of Long-Term Thermally Aged Cast Duplex Stainless Steels

被引：8
|
作者：
Li, Shilei [1 ]
Wang, Yanli [1 ]
Wang, Xitao [2 ,3 ]
机构：
[1] Univ Sci & Technol Beijing, State Key Lab Adv Met & Mat, Beijing 100083, Peoples R China
[2] Univ Sci & Technol Beijing, Collaborat Innovat Ctr Steel Technol, Beijing 100083, Peoples R China
[3] Qilu Univ Technol, Shandong Acad Sci, Adv Mat Inst, Shandong Prov Key Lab High Strength Lightweight M, Jinan 250353, Shandong, Peoples R China
来源：
METALS | 2019年 / 9卷 / 02期
基金：
中国国家自然科学基金;
关键词：
cast duplex stainless steels; thermal aging; tensile deformation; spinodal decomposition; MICROSTRUCTURAL CHANGES; AGING EMBRITTLEMENT; TEMPERATURE; PREDICTION;
D O I：
10.3390/met9020258
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Cast duplex stainless steel (CDSS) components suffer embrittlement after long-term thermal aging. The deformation and fracture behaviors of un-aged and thermally aged (at 400 degrees C for 20,000 h) CDSS were investigated using in situ scanning electron microscopy (SEM). The tensile strength of CDSS had a small increase, and the tensile fracture changed from ductile to brittle after thermal aging. Observations using in situ SEM indicated that the initial cracks appeared in the ferrite perpendicular to the loading direction after the macroscopic stress exceeded a critical value. The premature fracture of ferrite grains caused stress on the phase boundaries, leading the cracks to grow into austenite. The cleavage fracture of ferrite accelerated the shearing of austenite and reduced the plasticity of the thermally aged CDSS.
引用
收藏
页数：9
相关论文
共 50 条
  • [31] Microstructure evolution and impact fracture behaviors of Z3CN20-09M stainless steels after long-term thermal aging
    Li, S. L.
    Wang, Y. L.
    Zhang, H. L.
    Li, S. X.
    Zheng, K.
    Xue, F.
    Wang, X. T.
    JOURNAL OF NUCLEAR MATERIALS, 2013, 433 (1-3) : 41 - 49
  • [32] EFFECT OF LONG TERM AGING ON THE MICROSTRUCTURE AND MECHANICAL PROPERTIES OF CAST AUSTENITIC STAINLESS STEELS
    Li Shilei
    Wang Yanli
    Li Shuxiao
    Wang Xitao
    ACTA METALLURGICA SINICA, 2010, 46 (10) : 1186 - 1191
  • [33] Mechanical properties and kinetics of thermally aged Z3CN20.09M cast duplex stainless steel
    Liu, Tong-hua
    Wang, Wei
    Qiang, Wen-jiang
    Shu, Guo-gang
    INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, 2018, 25 (10) : 1148 - 1155
  • [34] New insights into the hardening and pitting corrosion mechanisms of thermally aged duplex stainless steel at 475 °C: A comparative study between 2205 and 2101 steels
    Silva, R.
    Vacchi, G. S.
    Kugelmeier, C. L.
    Santos, I. G. R.
    Mendes Filho, A. A.
    Magalhaes, D. C. C.
    Afonso, C. R. M.
    Sordi, V. L.
    Rovere, C. A. D.
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2022, 98 : 123 - 135
  • [35] The Microstructure and Mechanical and Corrosion Behaviors of Thermally Aged Z3CN20-09M Cast Stainless Steel for Primary Coolant Pipes of Nuclear Power Plants
    Xue, Fei
    Shi, Fangjie
    Zhang, Chuangju
    Zheng, Qiaoling
    Yi, Dawei
    Li, Xiuqing
    Li, Yefei
    COATINGS, 2021, 11 (08)
  • [36] Thermally induced fracture modeling during a long-term water injection
    Liu, Yuhao
    Yoshioka, Keita
    You, Tao
    Li, Hanzhang
    Zhang, Fengshou
    INTERNATIONAL JOURNAL OF ROCK MECHANICS AND MINING SCIENCES, 2025, 186
  • [37] THE MICROSTRUCTURE AND TENSILE FRACTURE BEHAVIOR OF LONG TERM THERMAL AGED Z3CN20-09M STAINLESS STEEL
    Zheng Kai
    Wang Yanli
    Li Shilei
    Lu Xuming
    Wang Xitao
    Xue Fei
    ACTA METALLURGICA SINICA, 2013, 49 (02) : 175 - 180
  • [38] Effects of long-term thermal aging on the stress corrosion cracking behavior of cast austenitic stainless steels in simulated PWR primary water
    Li, Shilei
    Wang, Yanli
    Wang, Hui
    Xin, Changsheng
    Wang, Xitao
    JOURNAL OF NUCLEAR MATERIALS, 2016, 469 : 262 - 268
  • [39] Thermal ageing on the deformation and fracture mechanisms of a duplex stainless steel by quasi in-situ tensile test under OM and SEM
    Wang, Y.
    Yao, Y. H.
    Wang, Z. P.
    Jin, Y. H.
    Zhang, X. L.
    Liu, J. N.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2016, 666 : 184 - 190
  • [40] The deformation and fracture behaviors of 316L stainless steels fabricated by spark plasma sintering technique under uniaxial tension
    Kale, Amol B.
    Bag, Atanu
    Hwang, Ji-Hyun
    Castle, Elinor G.
    Reece, Mike J.
    Choi, Shi-Hoon
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2017, 707 : 362 - 372
12345