ZrB2-SiC laminated ceramic composites

被引：36
作者：
Lu, Zhihui [1 ,2 ]
Jiang, Dongliang [1 ]
Zhang, Jingxian [1 ]
Lin, Qingling [1 ]
Huang, Zhengren [1 ]
机构：
[1] Chinese Acad Sci, Shanghai Inst Ceram, State Key Lab High Performance Ceram & Superfine, Shanghai 200050, Peoples R China
[2] Chinese Acad Sci, Grad Univ, Beijing 100049, Peoples R China
来源：
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY | 2012年 / 32卷 / 07期
基金：
中国国家自然科学基金;
关键词：
ZrB2-SiC; Mechanical properties; Laminated ceramic composites; DIBORIDE-SILICON CARBIDE; HIGH TEMPERATURE CERAMICS; MECHANICAL-PROPERTIES; ZIRCONIUM; OXIDATION; MICROSTRUCTURE;
D O I：
10.1016/j.jeurceramsoc.2011.04.020
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The oxidation behavior for ZrB2-20 vol% SiC (ZS20) and ZrB2-30 vol% SiC (ZS30) ceramics at 1500 degrees C was evaluated by weight gain measurements and cross-sectional microstructure analysis. Based on the oxidation results, laminated ZrB2-30 vol% SiC (ZS30)/ZrB2-25 vol% SiC (ZS25)/ZrB2-30 vol% SiC (ZS30) symmetric structure with ZS30 as the outer layer were prepared. The influence of thermal residual stress and the layer thickness ratio of outer and inner layer on the mechanical properties of ZS30/ZS25/ZS30 composites were studied. It was found that higher surface compressive stress resulted in higher flexural strength. The fracture toughness of ZS30/ZS25/ZS30 laminates was found to reach to 10.73 MPa m(1/2) at the layer thickness ratio of 0.5, which was almost 2 times that of ZS30 monolithic ceramics. (C) 2011 Elsevier Ltd. All rights reserved.
引用
收藏
页码：1435 / 1439
页数：5
相关论文
共 24 条
  • [1] High-strength zirconium diboride-based ceramics
    Chamberlain, AL
    Fahrenholtz, WG
    Hilmas, GE
    Ellerby, DT
    [J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2004, 87 (06) : 1170 - 1172
  • [2] LAMINAR CERAMIC COMPOSITES
    CHARTIER, T
    MERLE, D
    BESSON, JL
    [J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 1995, 15 (02) : 101 - 107
  • [3] A SIMPLE WAY TO MAKE TOUGH CERAMICS
    CLEGG, WJ
    KENDALL, K
    ALFORD, NM
    BUTTON, TW
    BIRCHALL, JD
    [J]. NATURE, 1990, 347 (6292) : 455 - 457
  • [4] Cutler R.A., 1991, CERAMICS GLASSES ENG, V4, P787
  • [5] The ZrB2 volatility diagram
    Fahrenholtz, WG
    [J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2005, 88 (12) : 3509 - 3512
  • [6] Refractory diborides of zirconium and hafnium
    Fahrenholtz, William G.
    Hilmas, Gregory E.
    Talmy, Inna G.
    Zaykoski, James A.
    [J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2007, 90 (05) : 1347 - 1364
  • [7] Oxidation behavior of zirconium diboride-silicon carbide at 1800°C
    Han, Jiecai
    Hu, Ping
    Zhang, Xinghong
    Meng, Songhe
    [J]. SCRIPTA MATERIALIA, 2007, 57 (09) : 825 - 828
  • [8] Improved processing, and oxidation-resistance of ZrB2 ultra-high temperature ceramics containing SiC nanodispersoids
    Hwang, Sung S.
    Vasiliev, Alexander L.
    Padture, Nitin P.
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2007, 464 (1-2): : 216 - 224
  • [9] Evaluation of ultra-high temperature ceramics for aeropropulsion use
    Levine, SR
    Opila, EJ
    Halbig, MC
    Kiser, JD
    Singh, M
    Salem, JA
    [J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2002, 22 (14-15) : 2757 - 2767
  • [10] Processing and properties of ZrB2-SiC composites obtained by aqueous tape casting and hot pressing
    Lue, Zhihui
    Jiang, Dongliang
    Zhang, Jingxian
    Lin, Qingling
    [J]. CERAMICS INTERNATIONAL, 2011, 37 (01) : 293 - 301
123