Synthesis of water-soluble Cu nanoparticles and evaluation of their tribological properties and thermal conductivity as a water-based additive

Efficient and sustainable use of water-based lubricants is essential for energy efficiency. Therefore, the use of water-lubricated mechanical systems instead of conventional oil lubricants is extremely attractive from the viewpoint of resource conservation. In this study, water-soluble Cu nanoparticles of size approximately 3 nm were prepared at room temperature (around 25 degrees C) via in-situ surface modification. The tribological behavior of the as-synthesized Cu nanoparticles as an additive in distilled water was evaluated using a universal micro-tribotester. The results show that the as-synthesized Cu nanoparticles, as a water-based lubricant additive, can significantly improve the tribological properties of distilled water. In particular, the lowest friction coefficient of 0.06 was obtained via lubrication with a concentration of 0.6 wt% of Cu nanoparticles in distilled water, which is a reduction of 80.6% compared with that obtained via lubrication with distilled water alone. It is considered that some Cu nanoparticles entered the contact area of the friction pairs to form a complex lubricating film and prevent direct contact of the friction pairs. Furthermore, some Cu nanoparticles in the solution accelerate the heat transfer process, which also results in good tribological properties.