Mechanical reliability of TWIP steel spot weldings

被引：16

作者：

Colombo, Tiago C. A. ^{[1
]}

Rego, Ronnie R. ^{[1
]}

Otubo, Jorge ^{[1
]}

de Faria, Alfredo R. ^{[1
]}

机构：

[1] Aeronaut Inst Technol ITA, Praca Marechal Eduardo Gomes 50, BR-12228900 Sao Jose Dos Campos, Brazil

来源：

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY | 2019年 / 266卷

关键词：

TWIP steels; MSS; Weld spots; Weibull; Residual stresses; FAILURE MODE TRANSITION; FUSION ZONE SIZE; RESIDUAL-STRESSES; WELDS; RECRYSTALLIZATION; DEFORMATION; SPECIMENS;

D O I：

10.1016/j.jmatprotec.2018.11.021

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

TWIP steel weld spots were produced by varying the following welding parameters: welding current, welding time and electrode clamping force. Hardness distributions along the weld spots cross section were obtained by Vickers microindentations. The mechanical strength and failure modes of the weld spots were assessed by tensile-shear tests. Weibull statistics was applied to statistically analyse the data from tensile-shear loading. The results highlighted the influence of welding parameters variations on the Vickers hardness and residual stress state. These properties have a positive correlation to the failure modes and so the mechanical reliability of the weld spots. Welds that failed in pullout mode and partial-interfacial failure mode have statistically higher load bearing capacity than those in interfacial failure mode. The combination of a welding current of 8 kA with a welding time of 16 cycles and an electrode clamping force of 2 IN showed to be the optimum parameters for the investigated TWIP steel weld spots. By using this optimum setup, it was possible to supress interfacial failure mode and to obtain pullout as the predominant failure mode, considerably increasing the mechanical reliability of the weld spots.

引用

页码：662 / 674

页数：13

共 41 条

[1] On Residual Stresses in Resistance Spot-Welded Aluminum Alloy 6061-T6: Experimental and Numerical Analysis [J].

Afshari, D. ;

Sedighi, M. ;

Karimi, M. R. ;

Barsoum, Z. .

JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2013, 22 (12) :3612-3619

[2]

Afshari D., 2012, P I MECH ENG B

[3]

Chao YJ, 2003, SCI TECHNOL WELD JOI, V8, P133, DOI 10.1179/136217103225008955

[4] Effects of Al addition on deformation and fracture mechanisms in two high manganese TWIP steels [J].

Chin, Kwang-Geun ;

Kang, Chung-Yun ;

Shin, Sang Yong ;

Hong, Seokmin. ;

Lee, Sunghak ;

Kim, Hyoung Seop ;

Kim, Kyung-hun ;

Kim, Nack J. .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2011, 528 (06) :2922-2928

[5] Recrystallization and texture [J].

Doherty, RD .

PROGRESS IN MATERIALS SCIENCE, 1997, 42 (1-4) :39-58

[6] Current issues in recrystallization: a review [J].

Doherty, RD ;

Hughes, DA ;

Humphreys, FJ ;

Jonas, JJ ;

Jensen, DJ ;

Kassner, ME ;

King, WE ;

McNelley, TR ;

McQueen, HJ ;

Rollett, AD .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1997, 238 (02) :219-274

[7]

Hauk V, 1997, STRUCTURAL AND RESIDUAL STRESS ANALYSIS BY NONDESTRUCTIVE METHODS, P3, DOI 10.1016/B978-044482476-9/50003-7

[8] A generalized Orowan model for cleavage fracture [J].

He, Jinshan ;

Lian, Junhe ;

Golisch, Georg ;

Jie, Xiaodong ;

Munstermann, Sebastian .

ENGINEERING FRACTURE MECHANICS, 2017, 186 :105-118

[9] Welding residual stresses as needed for the prediction of fatigue crack propagation and fatigue strength [J].

Hensel, J. ;

Nitschke-Pagel, T. ;

Ngoula, D. Tchoffo ;

Beier, H. -Th. ;

Tchuindjang, D. ;

Zerbst, U. .

ENGINEERING FRACTURE MECHANICS, 2018, 198 :123-141

[10]

Humphreys F.J., 2017, Recrystallization And Related Annealing Phenomena, Vthird

← 1 2 3 4 5 →