Enhancement of Field Emission Current of Iron Oxide Nanoemitters by in-situ Thermal Treatment

被引：0
|
作者：
Wu, J. Q. [1 ]
Chen, Jun [1 ]
Deng, S. Z. [1 ]
Xu, N. S. [1 ]
机构：
[1] Sun Yat Sen Univ, Sch Phys & Engn, State Key Lab Optoelect Mat & Technol, Guangdong Prov Key Lab Display Mat & Technol, Guangzhou 510275, Guangdong, Peoples R China
来源：
2011 24TH INTERNATIONAL VACUUM NANOELECTRONICS CONFERENCE (IVNC) | 2011年
关键词：
iron oxide; nanoemitters; field emission; thermal treatment; desorption; ALPHA-FE2O3; NANOFLAKES;
D O I：
暂无
中图分类号：
TM [电工技术]; TN [电子技术、通信技术];
学科分类号：
0808 ; 0809 ;
摘要：
Enhancement field emission current from iron oxide nanoemitters was observed after applying a in-situ thermal treatment process in vacuum. In one thermal treatment cycle, iron oxide nanoemitters were heated to 200 degrees C and kept for 2 hr. Comparison of I-V characteristics before and after thermal treatment shows that the field emission current were much enhanced from 60 mu A/cm(2) to 500 mu A/cm(2) at electric field of 10 MV/m. The threshold electric field decreased from 20 MV/m to 12.2 MV/m. Moreover, the enhancement was retained and the field emission current does not decrease to original level after cooling down. The emission current under different gas atmosphere were studied. The results show the observed enhancement was caused by the surface gas desorption, most likely the oxygen.
引用
收藏
页码：133 / 134
页数：2
相关论文
共 50 条
  • [41] Validation of satellite observed thermal emission with in-situ measurements over an urban surface
    Rigo, Gergely
    Parlow, Eberhard
    Oesch, David
    REMOTE SENSING OF ENVIRONMENT, 2006, 104 (02) : 201 - 210
  • [42] Application of microwave heating with iron oxide nanoparticles in the in-situ exploitation of oil shale
    Zhu, Jingyi
    Yang, Zhaozhong
    Li, Xiaogang
    Qi, Shuangyu
    Jia, Min
    ENERGY SCIENCE & ENGINEERING, 2018, 6 (05): : 548 - 562
  • [43] Preparation of Thermoplastic Magnetic Wood via Etherification and In-Situ Synthesis of Iron Oxide
    Matsumoto, Yusuke
    Teramoto, Yoshikuni
    Nishio, Yoshiyuki
    JOURNAL OF WOOD CHEMISTRY AND TECHNOLOGY, 2010, 30 (04) : 373 - 381
  • [44] Iron and steel refining with magnesium vapor produced in-situ by reduction of magnesium oxide
    Sano, M
    Okumura, K
    Shan, JY
    Yang, J
    SIXTH INTERNATIONAL CONFERENCE ON CLEAN STEEL, 2002, : 13 - 22
  • [45] IN-SITU DIRECT OBSERVATION OF CARBON NANOTUBE SYNTHESIS UNDER ELECTRIC FIELD AND THEIR FIELD EMISSION PERFORMANCE
    Vincent, Pascal
    Panciera, Federico
    Florea, Ileana
    Cojocaru, Costel
    Perisanu, Sorin
    Ayari, Anthony
    Chaste, Julien
    Legagneux, Pierre
    Purcell, Stephen T.
    2023 IEEE 36TH INTERNATIONAL VACUUM NANOELECTRONICS CONFERENCE, IVNC, 2023, : 120 - 121
  • [46] Enhancement of Carbon Oxides Hydrogenation on Iron-Based Nanoparticles by In-Situ Water Removal
    Bordet, Alexis
    Asensio, Juan Manuel
    Soulantica, Katerina
    Chaudret, Bruno
    CHEMCATCHEM, 2018, 10 (18) : 4047 - 4051
  • [47] In-situ studies of electron field emission of single carbon nanotubes inside the TEM
    Jin, CH
    Wang, JY
    Wang, MS
    Su, J
    Peng, LM
    CARBON, 2005, 43 (05) : 1026 - 1031
  • [48] In-situ opening aligned carbon nanotubes and applications for device assembly and field emission
    Zhu, Lingbo
    Hess, Dennis W.
    Wong, C. P.
    2006 OPTICS VALLEY OF CHINA INTERNATIONAL SYMPOSIUM ON OPTOELECTRONICS, 2006, : 12 - 18
  • [49] In-situ x-ray study of the thermal expansion of iron at multimegabar pressure
    Dubrovinsky, LS
    Saxena, SK
    Tutti, F
    Rekhi, S
    Le Bihan, T
    HIGH TEMPERATURES-HIGH PRESSURES, 1999, 31 (05) : 553 - 559
  • [50] In-situ growth of carbon nanotubes oriented vertically on vertical graphene for field emission
    Li, Yongjian
    Li, Xinlu
    Qin, Zhen
    Wang, Ronghua
    VACUUM, 2024, 228
12345