Dissimilar Laser Welding of Ti-6Al-4V to Ti-6Al-6V-2Sn

被引：2

作者：

Chiu, C. Y. ^{[1
]}

Lu, M. Y. ^{[1
]}

Tsay, L. W. ^{[1
]}

机构：

[1] Natl Taiwan Ocean Univ, Inst Mat Engn, Keelung 202, Taiwan

来源：

MANUFACTURING SCIENCE AND TECHNOLOGY, PTS 1-3 | 2011年 / 295-297卷

关键词：

Laser welding; Notched tensile strength; Ti-6Al-4V; Ti-6A16V-2Sn; POSTWELD HEAT-TREATMENT; CRACK GROWTH-BEHAVIOR; FRACTURE-TOUGHNESS; TITANIUM-ALLOYS; MICROSTRUCTURE;

D O I：

10.4028/www.scientific.net/AMR.295-297.2353

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Notched tensile strength (NTS) of the Ti-6Al-4V (Ti-6-4) to Ti-6A16V-2Sn (Ti-6-6-2) dissimilar laser yields were determined, which had been subjected to post-weld heat treatment (PWHT) over the temperature range of 482-704 degrees C. The results indicated for the weld with the PWFIT at 482 degrees C the fusion zone (FZ) and heat-affected zone (HAZ) showed a peak hardness, as compared with other welds at the counterpart regions, whereas, the weld with the PWHT at 704 degrees C had the lowest hardness among the welds. In all the welds, the FZ of the weld subjected to PWHT at 482 degrees C possessed the lowest NTS, while the as-welded and the weld with PWHT at 704 degrees C had superior NTS to others. The presence of grain boundary alpha, which promoted grain boundary shear, accounted for the typical features of mainly transgranular fracture with intergranular dimples of the welds.

引用

页码：2353 / 2357

页数：5

共 12 条

[1] BAESLACK WA, 1982, WELD J, V61, pS197
[2] Boyer R., 1994, MAT PROPERTIES HDB T, P637
[3] Chen S. J., 1982, METALL T A, V13A, P865
[4] LANCASTER JF, 1984, PHYSICS WELDING, P269
[5] Influence of processing on microstructure and mechanical properties of (α+β) titanium alloys
Lutjering, G
[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1998, 243 (1-2): : 32 - 45
[6] Mazumder J., 1980, METAL CONSTRUC, V12, P423
[7] Murthy KK, 1997, WELD J, V76, pS81
[8] Murthy KK, 1997, MATER SCI TECH SER, V13, P503, DOI 10.1179/026708397790302061
[9] IMPROVEMENT OF TI-6AL-4V FRACTURE-TOUGHNESS BY SUB-TRANSUS HEAT-TREATMENT
PLAZA, LM
IRISARRI, AM
GILNEGRETE, A
[J]. SCRIPTA METALLURGICA ET MATERIALIA, 1990, 24 (09): : 1765 - 1769
[10] SIMPSON RP, 1974, WELD J, V53, pS13

← 1 2 →