Biomimetic synthesis and characterization of carbon nanofiber/hydroxyapatite composite scaffolds

Three dimensional electrospun carbon nanofiber (CNF)/hydroxyapatite (HAp) composites were biomimetically synthesized in simulated body fluid (SBF). The CNFs with diameter of similar to 250 nm were first fabricated from electrospun polyacrylonitrile precursor nanofibers by stabilization at 280 degrees C for 2 h, followed by carbonization at 1200 degrees C. The morphology, structure and water contact angle (WCA) of the CNFs and CNF/HAp composites were characterized. The pristine CNFs were hydrophobic with a WCA of 139.6 degrees, resulting in the HAp growth only on the very outer layer fibers of the CNF mat. Treatment in NaOH aq. solutions introduced carboxylic groups onto the CNFs surfaces, and hence making the CNFs hydrophilic. In the SBF, the surface activated CNFs bonded with Ca2+ to form nuclei, which then easily induced the growth of HAp crystals on the CNFs throughout the CNF mat. The fracture strength of the CNF/HAp composite with a CNF content of 41.3% reached 67.3 MPa. Such CNF/HAp composites with strong interfacial bondings and high mechanical strength can be potentially useful in the field of bone tissue engineering. (C) 2012 Elsevier Ltd. All rights reserved.