Effects of stress ratio on crack growth rate and fatigue strength for high cycle and very-high-cycle fatigue of metallic materials

被引：39
|
作者：
Sun, Chengqi [1 ]
Lei, Zhengqiang [1 ]
Hong, Youshi [1 ]
机构：
[1] Chinese Acad Sci, Inst Mech, State Key Lab Nonlinear Mech, Beijing 100190, Peoples R China
来源：
MECHANICS OF MATERIALS | 2014年 / 69卷 / 01期
基金：
中国国家自然科学基金;
关键词：
Stress ratio; Crack growth rate; Fatigue strength; Very-high-cycle fatigue; Metallic materials; DRIVING-FORCE PARAMETER; LOAD RATIO; PROPAGATION BEHAVIOR; STEELS; LIFE; PREDICTION; MECHANISMS; THRESHOLD; FAILURE; CLOSURE;
D O I：
10.1016/j.mechmat.2013.10.007
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
This paper studies the effects of stress ratio R on crack growth rate and fatigue strength for high cycle and very-high-cycle fatigue of metallic materials. First, the effect of R on fatigue crack growth rate is analyzed, and the result shows that the effect of R on crack growth rate at near-threshold region and on Paris region is well expressed by a unified relation. Then, a model is developed for describing the fatigue crack growth rate with the effect of R in near-threshold region and Paris region. The model is verified by experimental data of metallic materials in literature. Finally, a formula is derived for the effect of R on fatigue strength. The estimated results are in good agreement with the experimental data for high cycle and very-high-cycle fatigue regime in literature. The comparison of the present result with Goodman diagram is also discussed. (C) 2013 Elsevier Ltd. All rights reserved.
引用
收藏
页码：227 / 236
页数：10
相关论文
共 50 条
  • [1] Correlation of crack growth rate and stress ratio for fatigue damage containing very high cycle fatigue regime
    Chengqi Sun
    Theoretical & Applied Mechanics Letters, 2012, 2 (03) : 11 - 14
  • [2] Correlation of crack growth rate and stress ratio for fatigue damage containing very high cycle fatigue regime
    Sun, Chengqi
    Hong, Youshi
    THEORETICAL AND APPLIED MECHANICS LETTERS, 2012, 2 (03) : 031004
  • [3] Effects of specimen size on fatigue life of metallic materials in high-cycle and very-high-cycle fatigue regimes
    Sun, C.
    Zhang, X.
    Liu, X.
    Hong, Y.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2016, 39 (06) : 770 - 779
  • [4] Effects of inclusion size and stress ratio on the very-high-cycle fatigue behavior of pearlitic steel
    Cong, Tao
    Qian, Guian
    Zhang, Guanzhen
    Wu, Si
    Pan, Xiangnan
    Du, Leiming
    Liu, Xiaolong
    INTERNATIONAL JOURNAL OF FATIGUE, 2021, 142
  • [5] A simulation on microstructure sensitivity to very-high-cycle fatigue behavior of metallic materials
    Lei, Zhengqiang
    Xie, Jijia
    Zhao, Aiguo
    Hong, Youshi
    ISAB-2010 - FIRST INTERNATIONAL SYMPOSIUM ON ARCHIMEDES BRIDGE, 2010, 4 : 225 - 232
  • [6] Method to estimate the fatigue-strength scatter of shafts in the high-cycle and very-high-cycle fatigue regimes
    Vetter, Sebastian
    Leidich, Erhard
    Hasse, Alexander
    ENGINEERING FAILURE ANALYSIS, 2023, 143
  • [7] Mechanisms of interior crack initiation in very-high-cycle fatigue of high-strength alloys
    Liu, Xiaolong
    Chen, Erqing
    Zeng, Fan
    Cong, Tao
    Domblesky, Joseph P.
    ENGINEERING FRACTURE MECHANICS, 2019, 212 : 153 - 163
  • [8] Crack growth rates and microstructure feature of initiation region for very-high-cycle fatigue of a high-strength steel
    Hu, Yuanpei
    Sun, Chengqi
    Hong, Youshi
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2018, 41 (08) : 1717 - 1732
  • [9] The nature and the mechanism of crack initiation and early growth for very-high-cycle fatigue of metallic materials - An overview
    Hong, Youshi
    Sun, Chengqi
    THEORETICAL AND APPLIED FRACTURE MECHANICS, 2017, 92 : 331 - 350
  • [10] Effects of Loading Frequency and Loading Type on High-Cycle and Very-High-Cycle Fatigue of a High-Strength Steel
    Hu, Yuanpei
    Sun, Chengqi
    Xie, Jijia
    Hong, Youshi
    MATERIALS, 2018, 11 (08)
12345