Microstructure and properties of A2017 alloy strips processed by a novel process by combining semisolid rolling, deep rolling, and heat treatment

被引:3
作者
Guan, Ren-guo [1 ]
Wang, Xiang [1 ]
Zhao, Zhan-yong [1 ]
Wang, Wei-wei [1 ]
Cao, Fu-rong [1 ]
Liu, Chun-ming [1 ]
机构
[1] Northeastern Univ, Coll Mat & Met, Shenyang 110819, Peoples R China
基金
中国国家自然科学基金;
关键词
aluminum alloys; semisolid rolling; heat treatment; microstructure; mechanical properties;
D O I
10.1007/s12613-013-0795-3
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
A novel short process for producing A2017 alloy strips with notable features of near net shape, saving energy, low cost, and high product performance was developed by combining semisolid rolling, deep rolling, and heat treatment. The microstructure and properties of the A2017 alloy strips were investigated by metallographic microscopy, scanning electron microscopy, transmission electron microscopy, X-ray diffraction, tensile testing, and hardness measurement. The cross-sectional microstructure of the A2017 alloy strips is mainly composed of near-spherical primary grains. Many eutectic phases CuAl2 formed along primary grain boundaries during semisolid rolling are crushed and broken into small particles. After solution treatment at 495A degrees C for 2 h the eutectic phases at grain boundaries have almost dissolved into the matrix. When the solution treatment time exceeds 2 h, grain coarsening happens. More and more grain interior phases precipitate with the aging time prolonging to 8 h. The precipitated particles are very small and distribute homogenously, and the tensile strength reaches its peak value. When the aging time is prolonged to 12 h, there is no obvious variation in the amount of precipitated phases, but the size and spacing of precipitated phases increase. The tensile strength of the A2017 alloy strips produced by the present method can reach 362.78 MPa, which is higher than that of the strips in the national standard of China.
引用
收藏
页码:770 / 778
页数:9
相关论文
共 20 条
[1]   Kinetics of coarsening and solid sphericity during reheating of ductile iron and Al alloys [J].
Babaghorbani, P. ;
Salarfar, S. ;
Nili-Ahmadabadi, M. .
SEMI-SOLID PROCESSING OF ALLOYS AND COMPOSITES, 2006, 116-117 :205-208
[2]  
Cai W.H., 2003, J NANCHANG U ENG TEC, V25, P13
[3]   Preparation of semi-solid aluminum alloy slurry poured through a water-cooled serpentine channel [J].
Chen, Zheng-zhou ;
Mao, Wei-min ;
Wu, Zong-chuang .
INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, 2012, 19 (01) :48-53
[4]   Near-liquidus molding of Mg-Al and Mg-Al-Zn alloys [J].
Czerwinski, F .
ACTA MATERIALIA, 2005, 53 (07) :1973-1984
[5]   Potential of the rheocasting process, demonstrated on different aluminum based alloy systems [J].
Grimmig, T. ;
Ovcharov, A. ;
Afrath, C. ;
Buenck, M. ;
Buehrig-Polaczek, A. .
SEMI- SOLID PROCESSING OF ALLOYS AND COMPOSITES, 2006, 116-117 :484-488
[6]   Microstructure evolution and properties of Mg-3Sn-1Mn (wt%) alloy strip processed by semisolid rheo-rolling [J].
Guan, R. G. ;
Zhao, Z. Y. ;
Zhang, H. ;
Lian, C. ;
Lee, C. S. ;
Liu, C. M. .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2012, 212 (06) :1430-1436
[7]   Semisolid die forging process, microstructures and properties of AZ31 magnesium alloy mobile telephone shells [J].
Guan, Ren-guo ;
Chen, Li-qing ;
Cao, Fu-rong ;
Zhao, Zhan-yong ;
Ren, Yong .
INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, 2011, 18 (06) :665-670
[8]   Twin roll casting of aluminum alloy strips [J].
Haga, T ;
Tkahashi, K ;
Ikawaand, M ;
Watari, H .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2004, 153 :42-47
[9]   Roll casting of Al-25mass%Si [J].
Haga, Toshio ;
Saito, Masayuki ;
Kumai, Shinji ;
Watari, Hisaki .
MANUFACTURING SCIENCE AND ENGINEERING, PTS 1-5, 2010, 97-101 :1057-+
[10]   An investigation on DC casting of a wrought aluminium alloy at below liquidus temperature by using melt conditioner [J].
Haghayeghi, R. ;
Zoqui, E. J. ;
Green, N. R. ;
Bahai, H. .
JOURNAL OF ALLOYS AND COMPOUNDS, 2010, 502 (02) :382-386