Microstructure and tribological behavior of multilayered CrN coating by arc ion plating

被引：30
|
作者：
Niu, Yunsong [1 ]
Wei, Jie [1 ]
Yu, Zhiming [1 ]
机构：
[1] Chinese Acad Sci, Inst Met Res, Lab Corros & Protect, Shenyang 110016, Peoples R China
来源：
SURFACE & COATINGS TECHNOLOGY | 2015年 / 275卷
关键词：
Tribological behavior; Columnar; Multilayered microstructure; Coefficient of friction; H/E; HIGH-TEMPERATURE OXIDATION; MECHANICAL-PROPERTIES; ABRASION RESISTANCE; RESIDUAL-STRESSES; FILMS; WEAR; TIN; SUBSTRATE; CHROMIUM; NI;
D O I：
10.1016/j.surfcoat.2015.04.045
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Multilayered CrN (M-CrN) coating was successfully prepared by arc ion plating method. The conventional CrN coatings were deposited under Ar + N-2 working pressures of 7.8 x 10(-1) Pa and 1.6 x 10(0) Pa, namely P-CrN and R-CrN respectively, for comparing the tribological behavior. M-CrN coating shows the multilayered microstructure. Transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS) measurements evidenced the different stoichiometry between the P-CrN and R-CrN layers. The experimental results show that wear resistance of the M-CrN coatings was much better than that of the conventional CrN coatings. Instead of bulk flake-off behavior, wear mechanism of the M-CrN coating is the micro-area detachment. That is because the multilayered microstructure can inhibit the formation of cracks extended into the substrate, with the high hardness, low coefficient of friction and high H/E value. (C) 2015 Elsevier B.V. All rights reserved.
引用
收藏
页码：332 / 340
页数：9
相关论文
共 50 条
  • [31] Study of the tribological behavior of an Ni electron brush plating layer on a base of an Arc sprayed coating
    Liu, XJ
    Xu, BC
    Ma, SI
    Chen, ZG
    WEAR, 1997, 211 (02) : 151 - 155
  • [32] High-temperature Oxidation and Tribological Behavior of AlTiYN Coatings by Arc Ion Plating
    Mo Jin-jun
    Wu Zheng-tao
    Gao Ze-cui
    Wang Qi-min
    CHINA SURFACE ENGINEERING, 2018, 31 (04) : 104 - 112
  • [33] Microstructure, Hardness and Oxidation Resistance of CrN and CrAIN Coatings Synthesized by Multi-arc Ion Plating Technology
    Cai, Zhihai
    Zhang, Ping
    Di, Yuelan
    ADVANCES IN BUILDING MATERIALS, PTS 1-3, 2011, 168-170 : 2430 - 2433
  • [34] High vacuum arc ion plating NiCrAlY coatings: Microstructure and oxidation behavior
    Shen, Mingli
    Zhao, Panpan
    Gu, Yan
    Zhu, Shenglong
    Wang, Fuhui
    CORROSION SCIENCE, 2015, 94 : 294 - 304
  • [35] Microstructural and tribological characterization of DLC coating by in-situ duplex plasma nitriding and arc ion plating
    Lan, Rui
    Ma, Zhifeng
    Wang, Chunji
    Lu, Guoying
    Yuan, Yanyan
    Shi, Changlun
    DIAMOND AND RELATED MATERIALS, 2019, 98
  • [36] Tribological performance of Zr-O-N coating in marine environment fabricated by arc ion plating
    Peng, Yuqing
    Yang, Linheng
    Wang, Yongxin
    Di, Chongqing
    Lu, Xiaojiang
    JOURNAL OF MATERIALS SCIENCE, 2024, 59 (28) : 13119 - 13132
  • [37] Effect of Electromagnetic Coil Voltage on Microstructure and Properties of TiAlN Coating Prepared by Arc Ion Plating
    Li, Hong
    Yang, Hong-Tai
    Lin, Song-Sheng
    Shi, Qian
    Wei, Chun-Bei
    Guo, Chao-Qian
    Su, Yi-Fan
    Tang, Peng
    Surface Technology, 2019, 48 (09): : 273 - 279
  • [38] Microstructure and Corrosion Resistance of TiN Coating on HSS by Pulsed Bias Cathodic Arc Ion Plating
    Yao, Xiaohong
    Tang, Bin
    Tian, Linhai
    Li, Xiaofang
    Ma, Yong
    ADVANCED MATERIAL SCIENCE AND TECHNOLOGY, PTS 1 AND 2, 2011, 675-677 : 1307 - 1310
  • [39] A comparative study on tribological behavior of TiN and TiAlN coatings prepared by arc ion plating technique
    Yoon, SY
    Kim, JK
    Kim, KH
    SURFACE & COATINGS TECHNOLOGY, 2002, 161 (2-3): : 237 - 242
  • [40] Formation of nanocrystalline microstructure in arc ion plated CrN films
    SeHun KWON
    KwangHo KIM
    Transactions of Nonferrous Metals Society of China, 2011, 21(S1) (S1) : 73 - 77
12345