Synthesis, characterization and heterogeneous catalytic application of copper integrated mesoporous matrices

被引:24
|
作者
Das, Swapan K. [1 ]
Mukherjee, Sanghamitra [1 ]
Lopes, Luis M. F. [2 ,3 ]
Ilharco, Laura M. [2 ,3 ]
Ferraria, Ana M. [2 ,3 ]
Botelho do Rego, Ana M. [2 ,3 ]
Pombeiro, Armando J. L. [1 ]
机构
[1] Univ Lisbon, Ctr Quim Estrut, Inst Super Tecn, P-1049001 Lisbon, Portugal
[2] Univ Lisbon, Ctr Quim Fis Mol, P-1049001 Lisbon, Portugal
[3] Univ Lisbon, Inst Super Tecn, IN Inst Nanosci & Nanotechnol, P-1049001 Lisbon, Portugal
关键词
LIQUID-PHASE OXIDATION; SELECTIVE OXIDATION; PEROXIDATIVE OXIDATION; CYCLOHEXANE OXIDATION; EFFICIENT CATALYST; SBA-15; PERFORMANCE; SILICA; VANADIUM; OXIDE;
D O I
10.1039/c3dt52510d
中图分类号
O61 [无机化学];
学科分类号
070301 ; 081704 ;
摘要
Ordered copper integrated mesoporous silicate catalysts (CuMSC) have been synthesized by the utilization of the amphiphilic tri-block copolymer pluronic F127 as a structure directing agent (SDA) under acidic aqueous conditions. The mesophase of the materials was investigated using small-angle powder X-ray diffraction and transmission electron microscopic (TEM) image analysis. N-2 adsorption-desorption studies show that the BET surface area of CuMSC (214-407 m(2) g(-1)) is lower than that of pure silica (611 m(2) g(-1)) and has smaller average pore dimensions (4.0-5.0 nm), both prepared following the same synthetic route. The reduction of pore size and surface area points to incorporation of copper within the silicate network. FEG-SEM results suggest that the materials have a plate-like morphology and are composed of very tiny nanoparticles. EDS surface chemical analysis was utilized for the detection of the distribution of Si, O and Cu in the matrix. The FT IR spectral study suggests the complete removal of the surfactants from the calcined materials and the presence of Si-O-Cu bonds for high nominal contents. X-ray photoelectron spectroscopy (XPS) and UV-vis reflectance spectra show the oxidation state of copper and coordination mode, respectively. These mesoporous materials display a good catalytic activity in the oxidation of cyclohexane to cyclohexanone and cyclohexanol in the presence of the green oxidant hydrogen peroxide. The maximum yield (cyclohexanone and cyclohexanol) was ca. 29% and the TON (turnover number) was 276 under optimal reaction conditions. The good catalytic activity could be attributed to the large surface area and the presence of a high number of active sites located at the surface of the material, as well as to its stability. The catalysts showed negligible loss of activity after five cycles.
引用
收藏
页码:3215 / 3226
页数:12
相关论文
共 50 条
  • [31] Ruthenium-Immobilized Periodic Mesoporous Organosilica: Synthesis, Characterization, and Catalytic Application for Selective Oxidation of Alkanes
    Ishito, Nobuhiro
    Kobayashi, Hirokazu
    Nakajima, Kiyotaka
    Maegawa, Yoshifumi
    Inagaki, Shinji
    Hara, Kenji
    Fukuoka, Atsushi
    CHEMISTRY-A EUROPEAN JOURNAL, 2015, 21 (44) : 15564 - 15569
  • [32] Direct synthesis, characterization and catalytic application of SBA-15 mesoporous silica with heteropolyacid incorporated into their framework
    Sheng, Xiaoli
    Kong, Jie
    Zhou, Yuming
    Zhang, Yiwei
    Zhang, Zewu
    Zhou, Shijian
    MICROPOROUS AND MESOPOROUS MATERIALS, 2014, 187 : 7 - 13
  • [33] Synthesis, characterization and catalytic application of mesoporous W-MCM-48 for the selective oxidation of cyclopentene to glutaraldehyde
    Yang, XL
    Dai, WL
    Gao, RH
    Chen, H
    Li, HX
    Cao, Y
    Fan, KN
    JOURNAL OF MOLECULAR CATALYSIS A-CHEMICAL, 2005, 241 (1-2) : 205 - 214
  • [34] Sol-gel synthesis and characterization of mesoporous iron-titanium mixed oxide for catalytic application
    Parida, K. M.
    Pradhan, Gajendra Kumar
    MATERIALS CHEMISTRY AND PHYSICS, 2010, 123 (2-3) : 427 - 433
  • [35] Synthesis and characterization of packed mesoporous tungsteno-silicates: application to the catalytic dehydrogenation of 2-propanol
    Trens, P
    Stathopoulos, V
    Hudson, MJ
    Pomonis, P
    APPLIED CATALYSIS A-GENERAL, 2004, 263 (01) : 103 - 108
  • [36] Synthesis, characterization and catalytic application of mesoporous molecular sieves SBA-15 functionalized with phosphoric acid
    Wu, Baoping
    Tong, Zhiwei
    Yuan, Xingdong
    JOURNAL OF POROUS MATERIALS, 2012, 19 (05) : 641 - 647
  • [37] Synthesis, characterization and catalytic application of mesoporous molecular sieves SBA-15 functionalized with phosphoric acid
    Baoping Wu
    Zhiwei Tong
    Xingdong Yuan
    Journal of Porous Materials, 2012, 19 : 641 - 647
  • [38] Synthesis, characterization and catalytic application of MCM-41 mesoporous molecular sieves containing Zn and Al
    Selvaraj, M
    Pandurangan, A
    Seshadri, KS
    Sinha, PK
    Lal, KB
    APPLIED CATALYSIS A-GENERAL, 2003, 242 (02) : 347 - 364
  • [39] Synthesis, characterization and catalytic application of RuII-ethylenediamine complex -: mesoporous silica as heterogeneous catalyst system in chemo-selective hydrogenation of α,β-unsaturated carbonyl compounds
    Ghosh, A
    Kumar, R
    MICROPOROUS AND MESOPOROUS MATERIALS, 2005, 87 (01) : 33 - 44
  • [40] Synthesis and characterization of mesoporous crystalline copper metal-organic frameworks for electrochemical energy storage application
    Omkaramurthy, B. M.
    Krishnamurthy, G.
    Foro, Sabine
    SN APPLIED SCIENCES, 2020, 2 (03):