Formation of nanostructured ω-Al 7Cu 2 Fe crystalline phase by the ball milling technique

被引：2

作者：

Pinto, M. Z. ^{[1
]}

Pillaca, M. ^{[1
]}

Landauro, C. V. ^{[1
]}

Quispe-Marcatoma, J. ^{[1
,2
]}

Rojas-Ayala, C. ^{[1
,2
]}

Pena Rodriguez, V. A. ^{[1
]}

Baggio-Saitovitch, E. ^{[2
]}

机构：

[1] UNMSM, Fac Ciencias Fis, Lima 14, Peru

[2] Urca, CBPF, BR-22290180 Rio De Janeiro, Brazil

来源：

HYPERFINE INTERACTIONS | 2014年 / 224卷 / 1-3期

关键词：

omega-Al7Cu2Fe phase; Nanostructured materials; X-ray diffraction; Mossbauer spectroscopy; QUASI-CRYSTAL; MOSSBAUER;

D O I：

10.1007/s10751-013-0868-8

中图分类号：

O64 [物理化学（理论化学）、化学物理学]; O56 [分子物理学、原子物理学];

学科分类号：

070203 ; 070304 ; 081704 ; 1406 ;

摘要：

Crystalline omega-Al7Cu2Fe bulk samples were prepared by arc furnace and then by means of milling, the average grain size of these samples is reduced to the nanometer scale. The structural and magnetic properties of the nanostructured omega-Al7Cu2Fe phase have been studied by X-ray diffraction employing Rietveld method, Mossbauer spectroscopy and vibrating sample magnetometry. The results indicate that the average grain size of the synthesized sample (omega-phase) rapidly decreases from 79 to 12 nm after 5 h of milling. Furthermore, the hyperfine parameters of the nanostructured samples are higher than the values for the bulk omega-phase. Magnetic measurements show a weak ferromagnetic behavior with M (s) = 0.46 emu.g (-aEuro parts per thousand 1) for the bulk omega-phase. After the milling process this value increases to M (s) = 1.50 emu.g (-aEuro parts per thousand 1) due to the formation and growth of a magnetic interstitial region after reducing the average grain size of the sample.

引用

页码：83 / 88

页数：6

共 37 条

[31] Synthesis and analysis of nanocrystalline β1-Cu3Al and β2-NiAl intermetallic-reinforced aluminum matrix composite by high energy ball milling
Hong-Hai Nguyen
Minh-Thuyet Nguyen
Won Joo Kim
Jin-Chun Kim
Metals and Materials International, 2017, 23 : 202 - 206
[32] Phase formation and thermal stability of (Zr1-xTix)O2 solid solution via a high-energy ball milling process
Kong, LB
Ma, J
Zhu, W
Tan, OK
JOURNAL OF ALLOYS AND COMPOUNDS, 2002, 335 (1-2) : 290 - 296
[33] OXIDATION BEHAVIOR OF THE PHASE ICOSAEDRAL QUASICRISTAL Al62, 2 Cu25,3 Fe12,5
Nascimento, L.
Agostinho, L. C. L.
Cavalcanti, B. F.
ACTA MICROSCOPICA, 2009, 18 (03): : 295 - 303
[34] Formation of calcium aluminoferrites in the ternary CaO-Al2O3-Fe2O3 system during solid-phase reactions
Samchenko, Svetlana, V
Korshunov, Andrey, V
CONSTRUCTION AND BUILDING MATERIALS, 2024, 455
[35] Accelerated precipitation due to mechanical milling of two-phase B2/L21 Fe30Ni20Mn20Al30
Wu, X.
Baker, I.
Wu, H.
Munroe, P. R.
JOURNAL OF ALLOYS AND COMPOUNDS, 2013, 559 : 97 - 100
[36] Preparation of super-high strength nanostructured B4C reinforced Al-2Cu aluminum alloy matrix composites by mechanical milling and hot press method: Microstructural, mechanical and tribological characterization
Alizadeh, Ali
Maleki, Mohammad
Abdollahi, Alireza
ADVANCED POWDER TECHNOLOGY, 2017, 28 (12) : 3274 - 3287
[37] Phase Formation and Critical Temperature of (Tl0.5Pb0.5)Sr2Ca(Cu2-xCx)O7-δ (x=0-0.100) Superconductor
Yusrianto, E.
Jannah, A. N.
Abd-Shukor, R.
SAINS MALAYSIANA, 2021, 50 (06): : 1775 - 1786

← 1 2 3 4 →