Performance of electro-plated and joined components for divertor application

A general challenge in divertor development, independently of design type and cooling medium water or helium, is the reliable and adapted joining of components. Depending on the design variants, the characteristics of the joints will be focused on functional or structural behavior to guarantee e.g. good thermal conductivity and sufficient mechanical strength. All variants will have in common that tungsten is the plasma facing material. Thus, material combinations to be joined will range from Cu base over steel to tungsten. Especially tungsten shows lacks in adapted joining due to its metallurgical behavior ranging from immiscibility over bad wetting up to brittle intermetallic phase formation. joining assisted by electro-chemical deposition of functional and filler layers showed that encouraging progress was achieved in wetting applying nickel interlayers. Nickel proved to be a good reference material but alternative elements (e.g. Pd, Fe) may be more attractive in fusion to manufacture suitable joints. Replacing of Ni as activator element by Pd for W/W or W/steel joints was achieved and joining with Cufiller was successfully performed. Manufactured joints were characterized applying metallurgical testing and SEM/EDX analyses demonstrating the applicability of Pd activator. First shear tests showed that the joints exhibit mechanical stability sufficient for technical application. (C) 2013 Elsevier B.V. All rights reserved.