Dielectric relaxation and ferroelectricity in Cd2Nb2O7 pyrochlore

The dielectric dispersion of Cd2Nb2O7 pyrochlore in a weak electric field was studied in a broad frequency range (100 Hz to 13 MHz) using the crystal samples slowly cooled (0.5 K/min) in the temperature interval from 300 to 80 K. As the temperature decreased down to T-c = 196 K and T-max similar to 190 K, the dielectric permittivity exhibited deviation from the Curie-Weiss law. It is suggested that this behavior is related to the development of a short-range correlation between microscopic polar regions formed at T --> T-max(+). The local order parameter q(T ) similar to <PiPj>(1/2) was calculated using the permittivity epsilon(')(T ) measured at various frequencies. The variation of this parameter is compared to that of the spontaneous polarization P-s(T ) determined from the measurements of a pyroelectric current in the external electric field E-dc = 0.95 kV/cm. In the frequency range from 100 Hz to 13 MHz, the dispersion of the dielectric response in the temperature region of 180-192 K is characteristic of a relaxator ferroelectric featuring a glasslike behavior. The parameters of this state were determined, including the activation energy of the polarization fluctuations (E-a approximate to 0.01 eV), the relaxation rate at T --> infinity (f(0) = 1.9 x 10(12) Hz), and the polarization fluctuation freezing temperature (T-f = 183 K). In Cd2Nb2O7 pyrochlore, in contrast to the known relaxator ferroelectrics of the PMN type studied previously, this state coexists with the normal ferroelectric state appearing at T-c. (C) 2002 MAIK "Nauka / Interperiodica".