Fracture behaviors under pure shear loading in bulk metallic glasses

被引:22
作者
Chen, Cen [1 ]
Gao, Meng [2 ]
Wang, Chao [2 ]
Wang, Wei-Hua [2 ]
Wang, Tzu-Chiang [1 ]
机构
[1] Chinese Acad Sci, Inst Mech, State Key Lab Nonlinear Mech, Beijing 100190, Peoples R China
[2] Chinese Acad Sci, Inst Phys, Beijing 100190, Peoples R China
基金
中国国家自然科学基金;
关键词
DUCTILE FRACTURE; MECHANISM; DEFORMATION; BRITTLE; FLOW;
D O I
10.1038/srep39522
中图分类号
O [数理科学和化学]; P [天文学、地球科学]; Q [生物科学]; N [自然科学总论];
学科分类号
07 ; 0710 ; 09 ;
摘要
Pure shear fracture test, as a special mechanical means, had been carried out extensively to obtain the critical information for traditional metallic crystalline materials and rocks, such as the intrinsic deformation behavior and fracture mechanism. However, for bulk metallic glasses (BMGs), the pure shear fracture behaviors have not been investigated systematically due to the lack of a suitable test method. Here, we specially introduce a unique antisymmetrical four-point bend shear test method to realize a uniform pure shear stress field and study the pure shear fracture behaviors of two kinds of BMGs, Zr-based and La-based BMGs. All kinds of fracture behaviors, the pure shear fracture strength, fracture angle and fracture surface morphology, are systematically analyzed and compared with those of the conventional compressive and tensile fracture. Our results indicate that both the Zrbased and La-based BMGs follow the same fracture mechanism under pure shear loading, which is significantly different from the situation of some previous research results. Our results might offer new enlightenment on the intrinsic deformation and fracture mechanism of BMGs and other amorphous materials.
引用
收藏
页数:10
相关论文
共 40 条
[1]   MECHANISM OF FRACTURE IN GLASSY MATERIALS CAPABLE OF SOME INELASTIC DEFORMATION [J].
ARGON, AS ;
SALAMA, M .
MATERIALS SCIENCE AND ENGINEERING, 1976, 23 (2-3) :219-230
[2]   PLASTIC-DEFORMATION IN METALLIC GLASSES [J].
ARGON, AS .
ACTA METALLURGICA, 1979, 27 (01) :47-58
[3]   Failure criterion for metallic glasses [J].
Chen, Y. ;
Jiang, M. Q. ;
Wei, Y. J. ;
Dai, L. H. .
PHILOSOPHICAL MAGAZINE, 2011, 91 (36) :4536-4554
[4]   Brittle versus ductile fracture mechanism transition in amorphous lithiated silicon: From intrinsic nanoscale cavitation to shear banding [J].
Ding, Bin ;
Li, Xiaoyan ;
Zhang, Xuan ;
Wu, Hui ;
Xu, Zhiping ;
Gao, Huajian .
NANO ENERGY, 2015, 18 :89-96
[5]  
Ewing J. A., 1900, PHIL T A, V195, P279
[6]   Mode II fracture behavior of a Zr-based bulk metallic glass [J].
Flores, Katharine M. ;
Dauskardt, Reinhold H. .
JOURNAL OF THE MECHANICS AND PHYSICS OF SOLIDS, 2006, 54 (11) :2418-2435
[7]   Hidden order in the fracture surface morphology of metallic glasses [J].
Gao, M. ;
Sun, B. A. ;
Yuan, C. C. ;
Ma, J. ;
Wang, W. H. .
ACTA MATERIALIA, 2012, 60 (20) :6952-6960
[8]  
Gao M., 2016, SCI REP, V6
[9]  
IOSIPESCU N, 1967, J MATER, V2, P537
[10]   Evolution of subsequent yield surfaces and elastic constants with finite plastic deformation. Part II: A very high work hardening aluminum alloy (annealed 1100 Al) [J].
Khan, Akhtar S. ;
Pandey, Amit ;
Stoughton, Thomas .
INTERNATIONAL JOURNAL OF PLASTICITY, 2010, 26 (10) :1421-1431