Effects of different fluorination routes on aramid fiber surface structures and interlaminar shear strength of its composites

被引:53
作者
Gao, Jie [1 ]
Dai, Yunyang [1 ]
Wang, Xu [1 ]
Huang, Jieyang [1 ]
Yao, Jin [1 ]
Yang, Jin [2 ]
Liu, Xiangyang [1 ]
机构
[1] Sichuan Univ, Coll Polymer Sci & Engn, State Key Lab Polymer Mat & Engn, Chengdu 610065, Peoples R China
[2] S China Univ Technol, State Key Lab Pulp & Paper Engn, Guangzhou 510640, Guangdong, Peoples R China
基金
中国国家自然科学基金;
关键词
PBIA; Surface modification; Direct fluorination; Interlaminar shear strength; OXYGEN PLASMA TREATMENT; INTERFACIAL PROPERTIES; EPOXY COMPOSITES; ADHESION; POLYMERS; BEHAVIOR;
D O I
10.1016/j.apsusc.2013.01.099
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
Poly-p-phenylene-benzimidazole-terephthalamide (PBIA) fiber was surface modified by direct fluorination under three different routes. The fiber was dried under vacuum to remove physisorbed water trapped on it and then fluorinated by the fluorine and oxygen gases or by the fluorine gas only. Results show that the interlaminar shear strength (ILSS) value of these two kinds of fluorinated fiber reinforced epoxy resin was 43.9 MPa and 51.0 MPa, which was improved about 14.0% and 32.5% compared with that of the virgin fiber (38.5 MPa), respectively. In the third route, the fiber was fluorinated by the fluorine and oxygen gases without removing physisorbed water, and the ILSS value decreased for nearly 31.2%, i.e. from 38.5 MPa to 26.5 MPa. X-ray photoelectron spectroscopy (XPS) showed that oxygen-containing and fluorine-containing chemical groups were introduced onto the fiber surface after fluorination, providing a stronger chemical bonding to polymeric matrices. Scanning electronic microscopy (SEM) indicated that the surface morphology of the fluorinated PBIA fiber varied with the different fluorination routes. A mass of compact micro groove structures was formed by the route that the fiber was dried to remove physisorbed water and then fluorinated with fluorine gas only. And these structures would markedly improve the ILSS of the composites. But, a mass of unstable flake surface structures was formed by the route that the fiber was fluorinated with the fluorine and oxygen gases without removing physisorbed water. And these structures would be the weak interface between the fiber and matrix and decrease the ILSS, even a lot of polar chemical groups were bonded onto the fiber surface as well. (C) 2013 Elsevier B.V. All rights reserved.
引用
收藏
页码:627 / 633
页数:7
相关论文
共 24 条
[1]   EFFECT OF DIRECT FLUORINATION ON THE BONDING PROPERTY OF ULTRA-HIGH MOLECULAR WEIGHT POLYETHYLENE [J].
Chen Yi ;
Zhang Peng ;
Wang Xu ;
Yang Jin ;
Liu Xiangyang .
ACTA POLYMERICA SINICA, 2011, (05) :543-547
[2]   Interfacial stress transfer in an aramid reinforced thermoplastic elastomer [J].
Coffey, A. B. ;
O'Bradaigh, C. M. ;
Young, R. J. .
JOURNAL OF MATERIALS SCIENCE, 2007, 42 (19) :8053-8061
[3]   Adhesion properties of polyamide-6 fibres treated by dielectric barrier discharge [J].
Dumitrascu, N. ;
Borcia, C. .
SURFACE & COATINGS TECHNOLOGY, 2006, 201 (3-4) :1117-1123
[4]   Direct fluorination of polymers - From fundamental research to industrial applications [J].
Kharitonov, A. P. .
PROGRESS IN ORGANIC COATINGS, 2008, 61 (2-4) :192-204
[5]   Modification of Ultra-High-Molecular Weight Polyethylene by Various Fluorinating Routes [J].
Kharitonov, Alexander P. ;
Simbirtseva, Galina V. ;
Bouznik, Vyacheslav M. ;
Chepezubov, Maxim G. ;
Dubois, Marc ;
Guerin, Katia ;
Hamwi, Andre ;
Kharbache, Hayat ;
Masin, Francis .
JOURNAL OF POLYMER SCIENCE PART A-POLYMER CHEMISTRY, 2011, 49 (16) :3559-3573
[6]   Practical applications of the direct fluorination of polymers [J].
Kharitonov, AP .
JOURNAL OF FLUORINE CHEMISTRY, 2000, 103 (02) :123-127
[7]   Direct fluorination - Useful tool to enhance commercial properties of polymer articles [J].
Kharitonov, AP ;
Taege, R ;
Ferrier, G ;
Teplyakov, V ;
Syrtsova, DA ;
Koops, GH .
JOURNAL OF FLUORINE CHEMISTRY, 2005, 126 (02) :251-263
[8]   Interfacial behavior of high performance organic fibers [J].
Leal, A. Andres ;
Deitzel, Joseph M. ;
McKnight, Steven H. ;
Gillespie, John W., Jr. .
POLYMER, 2009, 50 (05) :1228-1235
[9]   Effect of ultrasound on wettability between aramid fibers and epoxy resin [J].
Liu, L ;
Huang, YD ;
Zhang, ZQ ;
Yang, XB .
JOURNAL OF APPLIED POLYMER SCIENCE, 2006, 99 (06) :3172-3177
[10]   Tver' Fibres of the Armos Type: Manufacture and Properties [J].
N. N. Machalaba ;
N. N. Kuryleva ;
L. V. Okhlobystina ;
P. A. Matytsin ;
I. A. Andriyuk .
Fibre Chemistry, 2000, 32 (5) :319-324