White light emission from Dy3+ doped sodium-lead borophosphate glasses under UV light excitation

Sodium-lead borophosphate glasses doped with different Dy3+ concentrations have been prepared and characterized through, XRD, FTIR, optical absorption and photoluminescence techniques. FTIR spectrum indicates the presence of BO3 and PO4 structural units. The optical absorption spectrum has been studied at room temperature and several bands have been observed. These bands have been assigned to the ground state H-6(15/2) to several excited states. The bonding parameters have been evaluated based on the observed band positions. From the absorption spectrum, Judd-Ofelt (J-O) intensity parameters have been evaluated. By using J-O parameters radiative parameters such as transition probabilities, branching ratios and absorption cross section have been evaluated. The emission spectra have been studied for different concentrations of Dy3+ ions. The yellow/blue values due to F-4(9/2) -> H-6(13/2)/F-4(9/2) -> H-6(15/2) luminescence intensity ratios of Dy3+ ions, increase with increasing concentrations, suggesting higher asymmetry and more covalent bonding character between Dy and oxygen ligands. The chromaticity coordinates were calculated from emission spectra and analysed with Commission International deI'Eclarige Color diagram. The life time of the F-4(9/2) level has been measured and found to decrease with increase in Dy3+ ions concentration. Crown Copyright (C) 2013 Published by Elsevier B.V. All rights reserved.