Study on synthesis and performance of alite-strontium calcium sulfoaluminate cement

被引：7
|
作者：
Lu, Lingchao [1 ]
Wang, Shoude [1 ]
Li, Qiuying [1 ]
Cheng, Xin [1 ]
机构：
[1] Univ Jinan, Shandong Prov Key Lab Preparat & Measurement Bldg, Jinan, Peoples R China
来源：
ADVANCES IN CEMENT RESEARCH | 2012年 / 24卷 / 04期
基金：
中国国家自然科学基金;
关键词：
D O I：
10.1680/adcr.10.00054
中图分类号：
TU [建筑科学];
学科分类号：
0813 ;
摘要：
Synthesis conditions and performance of a novel alite-strontium calcium sulfoaluminate cement are reported: the clinker composition is modified from that of Portland cement. The mineral composition and the microstructure of the clinker were analysed by X-ray diffraction (XRD) analysis, scanning electron microscopy-energy dispersive X-ray spectrometry (SEM-EDS) and lithofacies. The results show that strontium calcium sulfoaluminate and the minerals of Portland cement clinker can coexist in one clinker system. The optimal composition of alite-strontium calcium sulfoaluminate clinker is as follows: strontium calcium sulfoaluminate 9% (mass %), C3S 59. 35%, C2S 14. 14%, C(3)A 7.50%, C(4)AF 10.00%. The content of strontium calcium sulfoaluminate produced during the sintering process at 1380 degrees C is high. The compressive strength of the cement prepared under the testing conditions reaches 30.5 MPa, 58.4 MPa and 122.2 MPa at 1 day, 3 days and 28 days curing ages, respectively.
引用
收藏
页码：187 / 192
页数：6
相关论文
共 50 条
  • [21] Performance of photocatalytic, carbonated calcium sulfoaluminate-belite cement
    Baral, Aniruddha
    Roesler, Jeffery R.
    CEMENT & CONCRETE COMPOSITES, 2022, 134
  • [22] STUDY ON DURABILITY OF ALITE-CALCIUM BARIUM SULPHOALUMINATE CEMENT
    Lu, Lingchao
    Wang, Shoude
    Zuo, Min
    Dong, Jiwen
    Cheng, Xin
    MICROSTRUCTURE RELATED DURABILITY OF CEMENTITIOUS COMPOSITES, VOLS 1 AND 2, 2008, 61 : 455 - 462
  • [23] Clinkering process and microstructure research on alite-sulfoaluminate portland cement clinker
    Guo, S. H.
    Qin, S. W.
    Zhu, X. Y.
    Chen, Y. A.
    Proceedings of the 6th International Symposium on Cement & Concrete and CANMET/ACI International Symposium on Concrete Technology for Sustainable Development, Vols 1 and 2, 2006, : 268 - 274
  • [24] The influence of gypsum ratio on the mechanical performance of slag cement accelerated by calcium sulfoaluminate cement
    Michel, Marie
    Georgin, Jean-Francois
    Ambroise, Jean
    Pera, Jean
    CONSTRUCTION AND BUILDING MATERIALS, 2011, 25 (03) : 1298 - 1304
  • [25] New applications of calcium sulfoaluminate cement
    Péra, J
    Ambroise, J
    CEMENT AND CONCRETE RESEARCH, 2004, 34 (04) : 671 - 676
  • [26] Durability of calcium sulfoaluminate cement concrete
    Tan, Bowen
    Okoronkwo, Monday U.
    Kumar, Aditya
    Ma, Hongyan
    JOURNAL OF ZHEJIANG UNIVERSITY-SCIENCE A, 2020, 21 (02): : 118 - 128
  • [27] Effect of calcium sulfoaluminate cement prehydration on hydration and strength gain of calcium sulfoaluminate cement-ordinary portland cement mixtures
    Ramanathan, Sivakumar
    Ben Halee
    Suraneni, Prannoy
    CEMENT & CONCRETE COMPOSITES, 2020, 112
  • [28] A New Belitic Calcium Sulfoaluminate Cement
    Deo, Omkar
    Bhuskute, Neel
    Paniagua, Julio
    Guijosa, Javier
    Rivera, Janeth
    Bescher, Eric P.
    JOURNAL OF MATERIALS IN CIVIL ENGINEERING, 2023, 35 (11)
  • [29] Effect of P2O5 on the Properties of Alite-Calcium Strontium Sulphoaluminate Cement
    Yin, Chaonan
    Lu, Lingchao
    Wang, Shoude
    EMERGING FOCUS ON ADVANCED MATERIALS, PTS 1 AND 2, 2011, 306-307 : 961 - 965
  • [30] Study on a high strength ternary blend containing calcium sulfoaluminate cement/calcium aluminate cement/ordinary Portland cement
    Zhang, Junjie
    Li, Guoxin
    Yang, Xiaofeng
    Ren, Shuangqian
    Song, Zhanping
    CONSTRUCTION AND BUILDING MATERIALS, 2018, 191 : 544 - 553
12345