Syntheses and properties of the Fe-Co/Fe3O4 ferrites

被引：2
作者：
Li, Shuimin [1 ]
Cui, Yuming [1 ]
Yang, Hua [1 ]
Chen, Yan [1 ,2 ]
机构：
[1] Jilin Univ, Coll Chem, Changchun 130012, Peoples R China
[2] Jilin Univ, State Key Lab Inorgan Synth & Prepart Chem, Changchun 130012, Peoples R China
来源：
JOURNAL OF PHYSICS AND CHEMISTRY OF SOLIDS | 2008年 / 69卷 / 10期
基金：
中国国家自然科学基金;
关键词：
Inorganic compounds; Magnetic materials; Nanostructures; Chemical synthesis; Magnetic properties;
D O I：
10.1016/j.jpcs.2008.04.042
中图分类号：
O6 [化学];
学科分类号：
0703 ;
摘要：
The Fe alloy-ferrite composites Fe-Co/Fe3O4 are synthesized by using disproportion of Fe (II) and reduction of Co (II) by Fe-0 in a concentrated and boiling KOH solution. The Fe alloy and ferrites are prepared in aqueous solution without any templet and surfactants at low temperature. Their structures and magnetic properties are investigated by X-ray diffractometer (XRD) and vibrating sample magnetometer (VSM). From the results of XRD, it is shown that the samples have b.c.c and f.c.c structure of Fe, and the spinel structures of the ferrite before calcinations; the samples have b.c.c and spinel structures after calcinations at 300 degrees C; and the samples have only f.c.c structure and the spinel structures calcined at 500 degrees C. Crown Copyright (C) 2008 Published by Elsevier Ltd. All rights reserved.
引用
收藏
页码：2471 / 2475
页数：5
相关论文
共 16 条
  • [11] Fe or Co-Fe alloy manganese ferrite composites
    Pourroy, G
    [J]. JOURNAL OF ALLOYS AND COMPOUNDS, 1998, 278 (1-2) : 264 - 269
  • [12] ADVANCES IN FINE MAGNETIC PARTICLES FOR HIGH-DENSITY RECORDING
    SUGITA, N
    MAEKAWA, M
    OHTA, Y
    OKINAKA, K
    NAGAI, N
    [J]. IEEE TRANSACTIONS ON MAGNETICS, 1995, 31 (06) : 2854 - 2858
  • [13] Role of the alloy and spinel in the catalytic behavior of Fe-Co/cobalt magnetite composites under CO and CO2 hydrogenation
    Tihay, F
    Roger, AC
    Pourroy, G
    Kiennemann, A
    [J]. ENERGY & FUELS, 2002, 16 (05) : 1271 - 1276
  • [14] Oxidation processes at the metal/oxide interface in CoFe2/CoFe2O4 bilayers deposited by pulsed laser deposition
    Viart, N
    Hassan, RS
    Ulhaq-Bouillet, C
    Mény, C
    Panissod, P
    Loison, JL
    Versini, G
    Huber, F
    Pourroy, G
    Verbeeck, J
    van Tendeloo, G
    [J]. ACTA MATERIALIA, 2006, 54 (01) : 191 - 196
  • [15] YOU WD, 1992, MAGNETIC RECORDING M, P290
  • [16] Synthes is and microwave magnetic properties of a-Fe/ferrite composites with sandwich structure
    Zhang, L.
    Deng, L. J.
    Zhou, P. H.
    [J]. JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2007, 312 (01) : 224 - 227
12