Numerical analysis for effects of shot peening on fatigue crack growth

被引：17
作者：
Liu, Jinxiang [1 ]
机构：
[1] Beijing Inst Technol, Sch Mech Engn, Beijing 100081, Peoples R China
来源：
INTERNATIONAL JOURNAL OF FATIGUE | 2013年 / 50卷
基金：
中国国家自然科学基金;
关键词：
Shot peening; Fatigue crack growth; Short cracks; Cohesive zone model; Finite elements; COHESIVE ZONE MODEL; PARAMETERS;
D O I：
10.1016/j.ijfatigue.2012.02.010
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
In the present work numerical analysis for effects of shot peening on fatigue crack growth are reported and discussed. Simulations reported in the present work use irreversible cohesive zone model and are based on experimental data for a Nickel-based superalloy. The capability of the cohesive zone model to catch the effects of short crack is investigated. The two-dimensional computations fit known experimental records in the CT specimen which confirms that the cohesive zone model has the potential for engineering application. The fatigue crack growth of shot-peened specimens are studied for different loading amplitudes and different shot peening intensities. The numerical results reveal that the crack initiation position and time depend not only on the shot peening intensity but also on the cyclic loading amplitude. Retardation of fatigue crack growth is more effective at lower loading amplitude for shot-peened specimens, and higher applied loading will eliminate the beneficial effects of shot peening. (C) 2012 Elsevier Ltd. All rights reserved.
引用
收藏
页码：101 / 108
页数：8
相关论文
共 50 条
[31]   Numerical analysis of fatigue crack growth of hip implant [J].
Sedmak, Aleksandar ;
Colic, Katarina ;
Grbovic, Aleksandar ;
Balac, Igor ;
Burzic, Meri .
ENGINEERING FRACTURE MECHANICS, 2019, 216
[32]   The influence of partial surface shot peening on fatigue crack growth behaviour of a high-strength ferritic steel [J].
Al-Turaihi, A. ;
Mehmanparast, A. ;
Brennan, F. .
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2018, 41 (03) :663-674
[33]   Direct measurement of shot velocity and numerical analysis of residual stress from pneumatic shot peening [J].
Ohta, Takahiro ;
Tsutsumi, Seiichiro ;
Ma, Ninshu .
SURFACES AND INTERFACES, 2021, 22
[34]   Numerical modeling the effects of overloading and underloading in fatigue crack growth [J].
Seifi, Rahman ;
Bahrami, Reza .
ENGINEERING FAILURE ANALYSIS, 2010, 17 (06) :1475-1482
[35]   Inertial effects on fatigue crack growth [J].
de Almeida, C. D. ;
Moresco, R. L. ;
Bittencourt, E. .
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2020, 43 (04) :711-720
[36]   The synergetic effects of shot peening and laser-shot peening on the microstructural evolution and fatigue performance of a medium carbon steel [J].
Zhang, Yating ;
Zhang, Kun ;
Hu, Zheng ;
Chen, Tianyu ;
Susmel, Luca ;
Wei, Bingchen .
INTERNATIONAL JOURNAL OF FATIGUE, 2023, 166
[37]   Numerical and experimental analysis of residual stresses for fatigue crack growth [J].
Wang, H ;
Buchholz, FG ;
Richard, HA ;
Jägg, S ;
Scholtes, B .
COMPUTATIONAL MATERIALS SCIENCE, 1999, 16 (1-4) :104-112
[38]   Effects of conventional shot peening, severe shot peening, re-shot peening and precised grinding operations on fatigue performance of AISI 1050 railway axle steel [J].
Unal, Okan ;
Maleki, Erfan ;
Karademir, Ibrahim ;
Husem, Fazil ;
Efe, Yusuf ;
Das, Turan .
INTERNATIONAL JOURNAL OF FATIGUE, 2022, 155
[39]   Fatigue strength improvement of an aluminum alloy with a crack-like surface defect using shot peening and cavitation peening [J].
Takahashi, Koji ;
Osedo, Hiroko ;
Suzuki, Takaya ;
Fukuda, Shinsaku .
ENGINEERING FRACTURE MECHANICS, 2018, 193 :151-161
[40]   Effects of shot peening with different coverage on surface integrity and fatigue crack growth properties of 7B50-T7751 aluminum alloy [J].
Qin, Zhi ;
Li, Bin ;
Zhang, Han ;
Wilfried, Tiako Youani Andre ;
Gao, Tao ;
Xue, Hongqian .
ENGINEERING FAILURE ANALYSIS, 2022, 133
12345