Optical properties of thin films of WO3, MoO3 and mixed oxides WO3/MoO3

Optical properties of thin films prepared by thermal evaporation of WO3, MoO3. and mixed oxides WO3/MoO3, have been studied. Satisfactory derivation of the refractive and absorption indices from the measured normal incidence transmittance of the films was achieved for the films of WO3 and MoO3. However, for films of the mixed oxides this was not possible, especially for the spectral region in which these films were absorbing; Rutherford backscattering spectrometry (RES) measurements on the films revealed that the films of WO3 and MoO3 were fairly uniform but the films prepared from the mixed oxides were chemically inhomogeneous. In fact, we were able to fit the RES data for the mixed-oxide films by assuming that the Mo content in the film decreased (while the W increased) along the direction of growth of the film (i.e. from the substrate side of the film to its surface).