Solution blowing nylon 6 nanofiber mats for air filtration

Solution blowing process is a new nanofiber fabricating method with high productivity. In the present study, nylon 6 nanofiber mats were solution blown and the effects of spinning conditions on nanofibers morphology were investigated. The fiber diameter ranged from 150 to 750 nm which was affected by solution concentration, gas pressure and solution feeding rate. The solution blown fibers were three-dimensional curly which made loose construction in bulk. The filtration performance of solution blown mats was evaluated. The tested solution blown nanofiber mats showed high filtration efficiency of 83.10 % to 93.45 % for 0.3 A mu m particles filtration and extremely low pressure drop of 15.37 to 30.35 Pa. The results indicate the solution blown nanofiber mats will find potential application of high efficiency and low resistance filter.