Long-time ablation protection of carbon/carbon composites with different-La2O3-content modified ZrC coating

被引：62

作者：

Jia, Yujun ^{[1
]}

Li, Hejun ^{[1
]}

Yao, Xiyuan ^{[1
]}

Sun, Jiajia ^{[1
]}

Zhao, Zhigang ^{[1
]}

机构：

[1] Northwestern Polytech Univ, State Key Lab Solidificat Proc, Xian 710072, Shaanxi, Peoples R China

来源：

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY | 2018年 / 38卷 / 04期

基金：

中国国家自然科学基金;

关键词：

Coating; Carbon/carbon composites; Lanthanum oxide; Long-time ablation; HIGH TEMPERATURE CERAMICS; CARBON-CARBON COMPOSITES; OXIDATION PROTECTION; C/C COMPOSITES; RESISTANCE; BEHAVIOR; SURFACE; PLASMA; PHASE; ZRB2;

D O I：

10.1016/j.jeurceramsoc.2017.09.050

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Long time oxidation protection at ultra-high temperatures or ablation protection has been a choke point for C/C composites. In this study, long time ablation protection of different-La2O3-content (5-30 vol.%) modified ZrC coating for SiC-coated carbon/carbon (C/C) composites was investigated. Results showed that ZrC coating with 15 vol.% La2O3 had good ablation resistance and could protect C/C composites for at least 700 s at 2160 degrees C. A high-thermal-stability and low-oxygen-diffusivity oxide scale containing m-ZrO2 particles and molten phases with La0.1Zr0.9O1.95 and La2Zr2O7 was formed during ablation, offering the ablation protection. La could erode grain boundaries of ZrO2 to refine ZrO2 by short-circuit diffusion and m-ZrO2 particles were retained due to less bulk diffusion than grain-boundary diffusion of La into ZrO2. The erosion resulted in the formation of molten phases containing fine nano-ZrO2, which served as viscous binder among m-ZrO2 particles and crack sealer for the oxide scale.

引用

页码：1046 / 1058

页数：13

共 33 条

[11] Ablation behavior of rare earth La-modified ZrC coating for SiC-coated carbon/carbon composites under an oxyacetylene torch [J].

Jia, Yujun ;

Li, Hejun ;

Feng, Lei ;

Sun, Jiajia ;

Li, Kezhi ;

Fu, Qiangang .

CORROSION SCIENCE, 2016, 104 :61-70

[12] Effect of surface ablation products on the ablation resistance of C/C-SiC composites under oxyacetylene torch [J].

Liu, Lei ;

Li, Hejun ;

Feng, Wei ;

Shi, Xiaohong ;

Wu, Heng ;

Zhu, Junliang .

CORROSION SCIENCE, 2013, 67 :60-66

[13] Effects of LaB6 addition on arc-jet convectively heated SiC-containing ZrB2-based ultra-high temperature ceramics in high enthalpy supersonic airflows [J].

Monteverde, Frederic ;

Alfano, Davide ;

Savino, Raffaele .

CORROSION SCIENCE, 2013, 75 :443-453

[14] Rheological behaviour of borosilicate composites with metallic and non-metallic dispersions [J].

Murthy, VSR ;

Murty, GS ;

Banuprakash, G ;

Das, S .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2000, 20 (11) :1717-1728

[15]

National standard committee of China, 1996, GJB323A96 NAT STNAD

[16] HfC nanowires to improve the toughness and oxidation resistance of Si-Mo-Cr/SiC coating for C/C composites [J].

Ren, Jincui ;

Zhang, Yulei ;

Hu, Heng ;

Zhang, Pengfei ;

Fei, Tian ;

Zhang, Leilei .

CERAMICS INTERNATIONAL, 2016, 42 (13) :14518-14525

[17] Oxidation protection of ultra-high temperature ceramic ZrxTa1-xB2-SiC/SiC coating prepared by in-situ reaction method for carbon/carbon composites [J].

Ren, Xuanru ;

Li, Hejun ;

Li, Kezhi ;

Fu, Qiangang .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2015, 35 (03) :897-907

[18] TaxHf1-xB2-SiC multiphase oxidation protective coating for SiC-coated carbon/carbon composites [J].

Ren, Xuanru ;

Li, Hejun ;

Fu, Qiangang ;

Li, Kezhi .

CORROSION SCIENCE, 2014, 87 :479-488

[19] Microscopy of structural ceramics [J].

Ruhle, M .

ADVANCED MATERIALS, 1997, 9 (03) :195-+

[20] Experimental investigation of passive/active oxidation behavior of SiC based ceramic thermal protection materials exposed to high enthalpy plasma [J].

Sakraker, Isil ;

Asma, Cem O. .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2013, 33 (02) :351-359

← 1 2 3 4 →