Long-Term Leaching Effects on CaO-Modified Iron Silicate Slag

Granulated iron silicate slag, a by-product of pyrometallurgical copper extraction, has excellent properties for construction applications. Slag modification with CaO enhances the application properties regarding pozzolanic reactivity, potentially extending slag use in the future. The slags' short-term leaching behavior has already been investigated with promising results, while the long-term leaching effects are less studied. Therefore, this study aims to determine the long-term leaching effects on CaO-modified iron silicate slags. The CaO-modifications were conducted during full-scale slag treatment operation. The slags were characterized and leached, and the remaining slags were investigated regarding the formation of secondary phases. The long-term leaching of main and trace elements was determined over 30 days using a dynamic leaching method corresponding to an extended time period. The leaching tests showed increased leaching of the main slag elements (Si, Ca). Zn and Cu showed peak leaching after four days of leaching, and the leaching of As and Sb decreased with the increasing CaO content in the samples. After dynamic leaching, secondary phases formed on the Cu-containing inclusions on the sample surfaces. Independent of the CaO content, the leaching of Cu was increased when subjected to external acidic and oxidating conditions using static pH titration at pH 5 in dilute nitric acid.