Progress towards all-chemical superconducting YBa2Cu3O7-coated conductors

Chemical solution deposition (CSD) has recently emerged as a very competitive technique for obtaining epitaxial films of high quality with controlled nanostructure. In particular, the all-CSD approach is considered to be one of the most promising approaches for cost-effective production of second-generation superconducting wires. The trifluoroacetate (TFA) route is a very versatile route for achieving epitaxial YBa2Cu3O7 (YBCO) layers with high critical currents. In this work, recent advances towards improvement of the performance of several conductor architectures based on the YBCO TFA process will be presented. We show that new improved anhydrous TFA precursors allow a significant shortening of the pyrolysis time (similar to 1.5 h), and we have increased the total film thickness in a single deposition using polymeric additives. On the other hand, further understanding of the YBCO nucleation and growth process has allowed us to obtain a controlled microstructure and high critical Currents (J(c) approximate to 4-5 MA cm(-2) and I-c approximate to 300 A cm(-1) width at 77 K). The growth conditions (CSD) and post-processing conditions (sputtering and CSD) for the underlying oxide cap and buffer layers (CeO2, BaZrO3, SrTiO3, La2Zr2O7, (La, Sr)MnO3) and of self-organized nanostructures (CeO2, BaZrO3) deposited by CSD have been investigated to obtain high-quality interfaces in multilayered systems. Different single-crystal or metallic substrates (YSZ-IBAD (yttrium stabilized zirconia-ion beam assisted deposition) and Ni-RABiT (rolling assisted biaxial texturing)) have been investigated and long (approximate to 10 m) CSD biaxially textured buffers (CeO2, La2Zr2O7) have been grown on Ni-RABiT substrates using a reel-to-reel system. High-performance TFA-YBCO-coated conductors have been obtained on vacuum-based buffer layers (I-c approximate to 140 A cm(-1) width) and on CSD buffer layers grown on IBAD YSZ-SS (stainless steel) substrates. Finally, we report on recent analysis of the magnetic granularity and vortex pinning properties of TFA-YBCO conductors.