Cracking and spallation of chromia and alumina scales during thermal cycling

被引：2

作者：

Osgerby, S ^{[1
]}

Evans, H

Saunders, S

机构：

[1] Natl Phys Lab, Ctr Mat Measurement & Technol, Teddington TW11 0LW, Middx, England

[2] Univ Birmingham, Sch Met & Mat, Birmingham B15 2TT, W Midlands, England

来源：

HIGH TEMPERATURE CORROSION AND PROTECTION OF MATERIALS 5, PTS 1 AND 2 | 2001年 / 369-3卷

关键词：

alumina; chromia; cracking; spallation; thermal cycling;

D O I：

10.4028/www.scientific.net/MSF.369-372.491

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Scale cracking and spallation behaviour under repeated thermal cycling has been studied for Haynes 214 and 20Cr25NNb for a spectrum of temperature ranges. Both alloys show an increase in the rate of mass gain after a small number of cycles in most cases. Continued cycling of Haynes 214 eventually results in spallation but this is not observed in the 20Cr25NiNb alloy. The increase in the rate of mass gain is consistent with predictions for FE models.

引用

页码：491 / 498

页数：8

共 50 条

[31] Prediction of Thermal Cracking During Construction of Massive Monolithic Structures [J].

Tyurina, Vasilina ;

Chepurnenko, Anton ;

Akopyan, Vladimir .

APPLIED SCIENCES-BASEL, 2025, 15 (03)

[32] Microscopic rearrangements in a granular column during compaction by thermal cycling [J].

Slotterback, Steven ;

Goff, Leonard ;

Toiya, Masahiro ;

Douglas, Jack ;

Van Hecke, Martin ;

Losert, Wolfgang .

POWDERS AND GRAINS 2009, 2009, 1145 :489-+

[33] Accumulation of Residual Strain in TiNi Alloy During Thermal Cycling [J].

Belyaev, S. ;

Resnina, N. ;

Sibirev, A. .

JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2014, 23 (07) :2339-2342

[34] Accumulation of Residual Strain in TiNi Alloy During Thermal Cycling [J].

S. Belyaev ;

N. Resnina ;

A. Sibirev .

Journal of Materials Engineering and Performance, 2014, 23 :2339-2342

[35] ASPECTS OF EVOLUTION OF METAL NANOSCALE CHARACTERISTICS DURING THERMAL CYCLING [J].

Zavorin, Alexander S. ;

Lyubimova, Lyudmila L. ;

Buvakov, Konstantin, V ;

Tashlykov, Alexander A. ;

Fisenko, Roman N. .

BULLETIN OF THE TOMSK POLYTECHNIC UNIVERSITY-GEO ASSETS ENGINEERING, 2020, 331 (08) :7-15

[36] Microstructural evidence for counter-diffusion of aluminum and oxygen during the growth of alumina scales [J].

Tolpygo, VK ;

Clarke, DR .

MATERIALS AT HIGH TEMPERATURES, 2003, 20 (03) :261-271

[37] Effect of thermal cycling and vibration on cracking in Sn-3.0Ag-0.5Cu solder bump [J].

Pongvittayapanu, Kittisak ;

Srisrual, Anusara ;

Fakpan, Kittichai .

MATERIALS TODAY-PROCEEDINGS, 2022, 52 :2372-2376

[38] Effects of polymeric binders on. the cracking behavior of silicon composite electrodes during electrochemical cycling [J].

Wang, Yikai ;

Dang, Dingying ;

Li, Dawei ;

Hu, Jiazhi ;

Zhan, Xiaowen ;

Cheng, Yang-Tse .

JOURNAL OF POWER SOURCES, 2019, 438

[39] Measurement of particulates formed during thermal protection system spallation in an arc-jet environment [J].

Price, K. J. ;

Martin, A. ;

Bailey, S. C. C. .

EXPERIMENTAL THERMAL AND FLUID SCIENCE, 2025, 167

[40] Simulation of plastic strain accumulation during thermal cycling of TiNi alloy [J].

Sibirev, Alexey ;

Resnina, Natalia ;

Volkov, Alexander ;

Belyaev, Sergey .

MATERIALS TODAY-PROCEEDINGS, 2017, 4 (03) :4743-4747

← 1 2 3 4 5 →