STRESS CORROSION CRACKING RESISTANCE OF ALUMINUM ALLOY 7000 SERIES AFTER TWO-STEP AGING

被引：2

作者：

Jegdic, Bore V. ^{[1
]}

Bobic, Biljana M. ^{[1
]}

Pavlovic, Milos K. ^{[2
]}

Alil, Ana B. ^{[3
]}

Putic, Slavisa S. ^{[4
]}

机构：

[1] Univ Belgrade, Inst Chem Technol & Met, Belgrade, Serbia

[2] Welding Inst, Belgrade, Serbia

[3] Univ Belgrade, Fac Technol & Met, Innovat Ctr, Belgrade 11000, Serbia

[4] Univ Belgrade, Fac Technol & Met, Belgrade 11000, Serbia

来源：

CHEMICAL INDUSTRY & CHEMICAL ENGINEERING QUARTERLY | 2015年 / 21卷 / 02期

关键词：

aluminum alloys; stress corrosion cracking; aging; mechanical properties; MG-CU ALLOY;

D O I：

10.2298/CICEQ140324024J

中图分类号：

O69 [应用化学];

学科分类号：

081704 ;

摘要：

The effect of one-step and a new (short) two-step aging process on the resistance to stress corrosion cracking of an aluminum alloy 7000 series was investigated, using slow strain rate test and fracture mechanics method The aging level in the tested alloy was evaluated by means of scanning electron microscopy and measurements of electrical resistivity. It was shown that the alloy after the new two-step aging is significantly more resistant to stress corrosion cracking. Values of tensile properties and fracture toughness are similar for both thermal states. Processes that take place at the crack tip have been considered. The effect of the testing solution temperature on the crack growth rate on the plateau was determined. Two values of the apparent activation energy were obtained. These values correspond to different processes that control crack growth rate on the plateau at higher and lower temperatures.

引用

页码：261 / 268

页数：8

共 50 条

[1] Effect of pre-strain and two-step aging on microstructure and stress corrosion cracking of 7050 alloy
Wang, D.
Ni, D. R.
Ma, Z. Y.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 494 (1-2): : 360 - 366
[2] Effects of step-quench and aging on mechanical properties and resistance to stress corrosion cracking of 7050 aluminum alloy
Ou, BL
Yang, JG
Yang, CK
MATERIALS TRANSACTIONS JIM, 2000, 41 (07): : 783 - 789
[3] Effect of two-step anodizing on corrosion and adhesion resistance of A5052 aluminum alloy
Hino, Makoto
Sugita, Shoei
Kuwano, Ryoichi
Nagata, Norihito
Yamashita, Michiru
Kanadani, Teruto
Keikinzoku/Journal of Japan Institute of Light Metals, 2024, 74 (08): : 346 - 351
[4] Effect of aging on fracture toughness and stress corrosion cracking resistance of forged 7475 aluminum alloy
Li, Hongying
Geng, Jinfeng
Dong, Xianjuan
Wang, Changjian
Zheng, Feng
JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2007, 22 (02): : 191 - 195
[5] Effect of aging on fracture toughness and stress corrosion cracking resistance of forged 7475 aluminum alloy
Hongying Li
Jinfeng Geng
Xianjuan Dong
Changjian Wang
Feng Zheng
Journal of Wuhan University of Technology-Mater. Sci. Ed., 2007, 22 : 191 - 195
[6] Effect of Aging on Fracture Toughness and Stress Corrosion Cracking Resistance of Forged 7475 Aluminum Alloy
李红英
Journal of Wuhan University of Technology(Materials Science Edition), 2007, (02) : 191 - 195
[7] Effect of natural aging time on stress corrosion cracking of aluminum alloy
Qian P.-W.
Deng Y.-L.
Zhang Z.
Zhao L.
Tang H.-Y.
Ye L.-Y.
Deng, Yun-Lai (dengylcsu@126.com), 1600, Central South University of Technology (27): : 1542 - 1550
[8] Enhancing aluminum corrosion resistance by two-step anodizing process
Bouchama, L.
Azzouz, N.
Boukrnouche, N.
Chopart, J. P.
Daltin, A. L.
Bouznit, Y.
SURFACE & COATINGS TECHNOLOGY, 2013, 235 : 676 - 684
[9] STRESS CORROSION CRACKING OF HIGH STRENGTH Al-Cu-Mg-Si ALLOYS AFTER TWO-STEP AGING.
Chen, Zailiang
Qian, Yourong
Xing, Shuyi
Key Engineering Materials, 1987, 20-28 (pt 1-4)
[10] Strengthening of aluminum alloy forgings for automotive suspension by two-step aging
Hori, Masayuki
Hirukawa, Kenichi
Nakano, Masashi
Tanaka, Masakazu
Okafuji, Yohei
R and D: Research and Development Kobe Steel Engineering Reports, 2020, 70 (02): : 7 - 11

← 1 2 3 4 5 →