Structural, magnetic and high-temperature thermoelectric properties of La0.4Bi0.4Ca0.2Mn1-xCoxO3 (0 ≤ x ≤ 0.3) perovskites

In this study, we have investigated the structural, magnetic and thermoelectric properties of La0.4Bi0.4Ca0.2Mn1-xCoxO3 (0 <= x <= 0.3) manganites. The crystallographic parameters of samples were determined by the Rietveld refinement of powder X-ray diffraction data. It was observed that Co doping results in change of crystal structures from orthorhombic (space group: Pbnm) to rhombohedral (space group: R-3c) symmetry. Scanning electron microscopy (SEM) images show smooth, clean and densified structures, depicting good crystallinity of samples. The zero field cooled (ZFC) and field cooled (FC) magnetization data were collected in the temperature range 5 to 300 K under an applied magnetic field of 0.1 Tesla. The analysis of temperature dependent magnetization data reveals all samples to be ferromagnetic with Curie temperatures around similar to 77 K. The magnetic hysteresis loops, collected at 5 K, show that the saturation magnetization (M-S) values decrease from 43 emu/g to 14 emu/g with increase in Co doping. The high temperature thermoelectric properties of all samples are characteristic of a semiconducting behavior, the small polaron hopping model fitting well with the temperature dependent electrical resistivity (rho) and thermopower (S) data. The thermopower values change sign from positive to negative as temperature is increased from 313 K to 680 K. The maximum thermoelectric power factor (PF = S-2/rho) obtained for x = 0.3 sample at 313 K is 4.60 lW/mK(2), is much higher than for the undoped sample. (C) 2017 Elsevier B.V. All rights reserved.